Ultracapacitor electrode with controlled sulfur content
View Patent ↗Particles of active electrode material are made by blending mixing a mixture of activated carbon and binder. In selected implementations, sulfur level in the activated carbon is relatively low and the binder is inert. For example, sulfur content of the activated carbon and the resultant mixture is below 300 ppm and in other implementations, below 50 ppm. The electrode material may be attached to a current collector to obtain an electrode for use in various electrical devices, including a double layer capacitor. The electrode decreases current leakage of the capacitor.
1. A method of making an active electrode material, the method comprising: providing activated carbon with a sulfur content in the range of about 0 and about 300 parts per million; providing binder; and, mixing the activated carbon and the binder to obtain a mixture of active electrode material.
2. A method in accordance with claim 1 , wherein the providing activated carbon operation further comprises providing activated carbon with a sulfur content not exceeding about 50 parts per million.
3. A method in accordance with claim 1 , wherein the mixture of active electrode material has a sulfur content in the range of about 0 and about 300 parts per million.
4. A method in accordance with claim 1 , wherein the operation of providing the activated carbon includes providing activated carbon in amount of between about 80 and about 97 percent by weight, and wherein the operation of providing the binder includes providing binder in amount of between about 3 and about 20 percent by weight.
5. A method in accordance with claim 1 , further comprising providing an additional additive component having a sulfur content not exceeding an amount whereby the mixture of active electrode material has a sulfur content in the range of about 0 and about 300 parts per million.
6. A method in accordance with claim 5 , wherein the additional additive component is conductive carbon.
7. A method in accordance with claim 1 , wherein the binder includes PTFE.
8. A method in accordance with claim 1 , wherein the operation of mixing is performed without processing additives.
9. A method in accordance with claim 1 , wherein the operation of mixing includes dry blending the activated carbon and the binder.
10. A method of making an active electrode material, the method comprising: providing activated carbon with a sulfur content in the range of about 0 and about 300 parts per million; providing low contamination level conductive carbon particles; providing binder; and, mixing the activated carbon, the conductive carbon, and the binder to obtain a mixture such that the mixture has a sulfur content in the range of about 0 and about 300 parts per million.
11. A method in accordance with claim 10 , wherein the providing activated carbon operation further comprises providing activated carbon with a sulfur content not exceeding about 50 parts per million.
12. A method in accordance with claim 11 , wherein the mixture has a sulfur content not exceeding about 50 parts per million.
13. A method in accordance with claim 10 , wherein the providing conductive carbon operation further comprises providing conductive carbon with a sulfur content not exceeding about 300 parts per million.
14. A method in accordance with claim 13 , wherein the providing conductive carbon operation further comprises providing conductive carbon with a sulfur content not exceeding about 50 parts per million, and wherein the mixture has a sulfur content not exceeding about 50 parts per million.