Aqueous epoxy resin compositions
Curable, aqueous epoxy resin composition, comprising a) an epoxy compound, b) an aminic curing agent which is an aqueous solution of a product from the reaction between i) an adduct between a polyamine and a liquid glycidyl ether which is not a glycidyl ether of a polyalkylene glycol, and ii) an epoxidized polyalkylene glycol, and c) from 0.5 to 15 wt.-%, based on the sum of the components b) and c), of a compound of the general formula (I) whereby R 1 =—H or —C 4 H 9 , and x=1, 2, 3 or 4, providing due to the presence of component c) an adjustable and recognizable end of pot life during application, for example coating, adhesive, as flooring, casting, tooling or encapsulating.
1. Curable, aqueous epoxy resin composition, comprising
a) an epoxy compound,
b) an aminic curing agent which is an aqueous solution of a product from the reaction between i) an adduct between a polyamine and a liquid glycidyl ether consisting of glycidyl compounds based on bisphenol A and/or bisphenol F, and ii) an epoxidized polyalkylene glycol, and
c) from 0.5 to 15 wt. %, based on the sum of the components b) and c), of a compound of the general formula (I)
whereby
R 1 =—H or —C 4 H 9 , and x=1, 2, 3 or 4.
2. A composition according to claim 1 , wherein component c) is used in an amount of from 3 to 6% per weight, based on the sum of components b) and c).
3. A composition according to claim 1 wherein component a) has on average more than one epoxy group per molecule.
4. A composition according to claim 1 wherein component a) is used in aqueous dispersed form.
5. A composition according to claim 1 wherein component a) is mixture of a glycidyl compound based on bisphenol A, bisphenol F or a novolac with a reactive diluent.
6. A composition according to claim 1 wherein component c) is a compound of formula (I), wherein R 1 =—H, and x=1, 2, or 3.
7. A composition according to claim 6 , wherein component c) is diethylene glycol monobutyl ether.
8. Cured product, obtained from full cure of a composition according to claim 1 .
9. A method for adjusting the pot life of an aqueous epoxy resin composition comprising adding to the composition a compound of the general formula (I)
whereby
R 1 =—H or —C 4 H 9 , and x=1, 2, 3 or 4 and wherein the composition includes
a) an epoxy compound, and
b) an aminic curing agent which is an aqueous solution of a product from the reaction between i) an adduct between a polyamine and a liquid glycidyl ether consisting of glycidyl compounds based on bisphenol A and/or bisphenol F, and ii) an epoxidized polyalkylene glycol.