Method for the desulfurization of fuels and highly active nickel carrier catalyst based on aluminum oxide suitable for said method
View Patent ↗A highly active nickel carrier catalyst based on aluminium oxide has a nickel content of approximately 20 to 70 wt.-% (as Ni) and optionally comprises a bonding agent and optionally a promoter, selected from the compounds of Mg, Ti, Pb, Pt, Ba, Ca and/or Cu, wherein the size of the Ni crystallites in the reduced state is in the range of approximately 3.5 to 4.5 nm and the distortion factor of the Ni crystallites is approximately 2 to 5%. In a method for the reduction of the content of sulphur compounds in hydrocarbon-based fuels by selective adsorption of the sulphur compounds on a nickel catalyst, a nickel catalyst based on aluminium oxide is used, particularly the nickel catalyst described above. A nickel catalyst based on aluminium oxide may be used for reducing the sulphur compound content in hydrocarbon-based fuels by selective adsorption of the sulphur compounds on said catalyst and/or for the hydrogenation of aromatic compounds.
1. Method for reducing the level of sulfur compounds in hydrocarbon-based fuels or fuel fractions, comprising the following step: reducing the level of sulphur compounds in hydrocarbon-based fuels or fuel fractions by selectively adsorbing the sulphur compounds on a catalyst, which catalyst has previously been used for hydrogenating aromatics in another hydrocarbon fraction,
wherein the catalyst comprises a highly active, aluminum oxide-based, nickel support catalyst comprising approximately 20 to 70 wt.-% nickel (as Ni), wherein the size of the Ni crystallites in a reduced state is in the range of approximately 3.5 to 4.5 nm, and wherein the nickel support catalyst essentially contains no silicon compounds.
2. Method according to claim 1 , wherein the catalyst further comprises a binder and/or a promoter, selected from the group consisting of Mg, Ti, Pd, Pt, Ba, Ca and Cu.
3. Method according to claim 1 , characterized in that the catalyst has a nickel content of approximately 30 to 70 wt.-% (as Ni).
4. Method according to claim 1 , characterized in that the catalyst has a specific BET surface area (total surface area of Ni and support) of approximately 180 to 250 m 2 /g.
5. Method according to claim 1 , characterized in that the specific surface of the Ni crystallites is approximately 70 to 90 m 2 /g.
6. Method according to claim 1 , characterized in that the pore radii distribution of the catalyst is:
7500- 875 nm: 0- 45 mm 3 /g
875- 40 nm: 2- 20 mm 3 /g
40- 7 nm: 20- 70 mm 3 /g, and
7- 3.5 nm: 100- 400 mm 3 /g.
7. Method according to claim 1 , characterized in that the catalyst is used in pellet form.
8. Method according to claim 7 , characterized in that the pellets do not contain an acid binder.
9. Method according to claim 7 , characterized in that the pellets further comprise graphite as a binder.
10. Method according to claim 1 , characterized in that the total pore volume of the catalyst in the reduced state is approximately 150 to 450 mm 3 /g.
11. Method according to claim 1 wherein the hydrocarbon-based fuels or fuel fractions comprises diesel.