POLYPROPYLENE FOR USE IN BOPP APPLICATIONS
The present invention relates to polypropylene compositions having a broad molecular weight distribution with a relatively high amount of xylene soluble material. The compositions have an Mw/Mn of five or greater, but preferably greater than 5.5 and more preferably greater than 6.0. The compositions have xylene solubles from 5.0 to 8.0 percent by weight, preferably from 5.5 to 8.0 percent by weight, and more preferably 6.0 to 7.5 percent by weight. The polymers of the present invention are particularly well suited for biaxially oriented polypropylene applications.
1 . A multi-reactor homopolymer propylene based polymer having an Mw/Mn greater than 5 and having a xylene soluble content from 5 to 8 percent by weight.
2 . The polymer of claim 1 wherein the xylene soluble content is from 5.5 to 8.0 percent by weight.
3 . The polymer of claim 2 , wherein the xylene soluble content is from 6.0 to 7.5 percent by weight.
4 . The polymer of claim 1 further characterized by having an isotacticity (% mm) less than 92.5%.
5 . The polymer of claim 1 wherein the Mw/Mn is greater than 5.5.
6 . The polymer of claim of claim 5 wherein the Mw/Mn is greater than 6.0.
7 . The polymer of claim 1 wherein the polymer comprises from 0 to 1.5 percent by weight of units derived from ethylene.
8 . The polymer of claim 1 wherein the polymer comprises from 0 to 1.0 percent by weight of units derived from ethylene.
9 . The polymer of claim 1 wherein the polymer comprises from 0 to 0.7 percent by weight of units derived from ethylene.
10 . The polymer of claim 1 wherein the polymer is further characterized by having a melt flow rate as determined according to ASTM D1238, 230° C., 2.16 kg of 1.0 to 4.0 g/10 min.
11 . An improved method for producing biaxially oriented polypropylene film comprising
a. selecting a multi-reactor homopolymer propylene based polymer having a Mw/Mn greater than 5 and having a xylene soluble content of from 5 to 8 percent by weight;
b. extruding the propylene based polymer into a flat sheet
c. forming a film using a tenter biaxially oriented film process.
12 . The method of claim 11 characterized in that the tenter biaxially oriented film process is operated at a line speed of at least 400 m/min.
13 . The method of claim 11 where the polymer comprises from 0 to 1.5 percent by weight of units derived from ethylene.
14 . A homopolymer polypropylene based polymer having an Mw/Mn greater than 6 and xylene solubles greater than 6.4% by weight.
15 . The polymer of claim 15 wherein the polymer comprises from 0 to 1.5 percent by weight of units derived from an alpha olefin other than propylene.