Carrier film for fuel cell production process and its production method
View Patent ↗To provide a carrier film for a fuel cell production process which is excellent in a recycling property and sufficient handling property in the fuel cell production process. A carrier film for a fuel cell production process, which is made of a fluororesin and has a tensile elastic modulus of at least 1,500 MPa in the machine direction, as measured in accordance with ASTM D882, and a tensile modulus of at least 100 MPa in the machine direction at 150° C., and which preferably has a thickness of from 10 to 300 μm.
1. A coated carrier film for a fuel cell production process, comprising:
a coating of a layer of a fuel cell or a membrane component of a fuel cell; and
a carrier film consisting of a biaxially stretched fluororesin; wherein
a tensile elastic modulus of the carrier film is at least 1,500 Mpa in the machine direction, as measured in accordance with ASTM D882,
a tensile elastic modulus of the carrier film is at least 100 MPa in the machine direction at 150° C., and
the coating is releasable from the carrier film.
2. The coated carrier film for a fuel cell production process according to claim 1 , wherein
the fluororesin carrier film is biaxially stretched in the machine direction and the transverse direction.
3. The coated carrier film for a fuel cell production process according to claim 2 , wherein after the biaxial stretching, the fluororesin carrier film is further subjected to a thermosetting treatment.
4. The coated carrier film for a fuel cell production process according to claim 2 , wherein a stretching temperature is at least the glass transition point and less than the melting point of the fluororesin of the fluororesin carrier film.
5. The coated carrier film for a fuel cell production process according to claim 2 , wherein a stretch ratio in the machine direction is from 2 to 8 times.
6. The coated carrier film for a fuel cell production process according to claim 1 , wherein a thickness of the fluororesin carrier film is from 10 to 300 μm.
7. The coated carrier film for a fuel cell production process according to claim 1 , wherein the fluororesin is an ethylene/tetrafluoroethylene copolymer.
8. A method for producing a coated carrier film for a fuel cell production process, comprising:
biaxially stretching a fluororesin film in the machine direction and the transverse direction to obtain a fluororesin carrier film, having a tensile elastic modulus of at least 1,500 Mpa in the machine direction, as measured in accordance with ASTM D882 and a tensile elastic modulus of at least 100 MPa in the machine direction at 150° C.; and
coating the obtained fluororesin carrier film with a layer of a fuel cell or a membrane member of a fuel cell.
9. The method for producing a coated carrier film for a fuel cell production-process according to claim 8 , further comprising after the or biaxial stretching, a thermal setting treatment of the fluororesin film.
10. The method for producing a coated carrier film for a fuel cell production-process according to claim 8 , wherein a stretching temperature is at least the glass transition point and less than the melting point of the fluororesin of the fluororesin carrier film.
11. The method for producing a coated carrier film for a fuel cell production-process according to claim 8 , wherein a stretch ratio in the machine direction is from 2 to 8 times and a stretch ratio in the transverse direction is 1 to 8 times.
12. A coated carrier film for production of a fuel cell, comprising:
an ion exchange resin coating; and
a carrier film consisting of a biaxially stretched fluororesin; wherein
a tensile elastic modulus of the carrier film is at least 1,500 Mpa in the machine direction, as measured in accordance with ASTM D882,
a tensile elastic modulus of the carrier film is at least 100 MPa in the machine direction at 150° C., and
the ion exchange resin coating is releasable from the carrier film.
13. The coated carrier film for production of a fuel cell according to claim 12 , wherein after the biaxial stretching, the fluororesin carrier film is further subjected to a thermosetting treatment.
14. The coated carrier film for production of a fuel cell according to claim 12 , wherein a stretching temperature is at least the glass transition point and less than the melting point of the fluororesin of the fluororesin carrier film.
15. The coated carrier film for production of a fuel cell, according to claim 12 , wherein a stretch ratio in the machine direction is from 2 to 8 times and a stretch ratio in the transverse direction is 1 to 8 times.
16. The coated carrier film for production of a fuel cell, according to claim 12 , wherein a thickness of the fluororesin carrier film is from 10 to 300 μm.
17. The coated carrier film for production of a fuel cell, according to claim 12 , wherein the fluororesin is an ethylene/tetrafluoroethylene copolymer.