Optical film and manufacturing method therefor, antiglare film, optical layer-attached polarizer, and dispaly apparatus

1. An optical film comprising:

a base member; and

an optical layer disposed on the base member, the optical layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin on the base member, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

2. The optical film according to claim 1 , wherein a ratio R (=D/T×100, where T is the average thickness of the optical layer and D is the average diameter of the microparticles) is 30% or more and 70% or less.

3. The optical film according to claim 1 , wherein the microparticles are mainly composed of a cross-linking poly(meth)acrylate copolymer having an acryl content of 55 wt % to 85 wt %.

4. The optical film according to claim 1 , wherein a sum of transmitted image clarity measured with optical combs having a width of 0.125 mm, 0.5 mm, 1.0 mm, and 2.0 mm is 230 or more.

5. The optical film according to claim 1 , wherein the resin contains 3 wt % or more and 20 wt % or less of a polymer and 80 wt % or more and 97 wt % or less of an oligomer and/or a monomer.

6. The optical film according to claim 5 , wherein the resin contains 3 wt % or more and 20 wt % or less of the polymer and 80 wt % or more and 97 wt % or less of the oligomer.

7. A method for making an optical film comprising:

applying a coating material containing microparticles and a resin on a base member;

drying the coating material to create convections in the coating material and distributing the microparticles by the convections so that the microparticles are distributed densely in some parts and sparsely in other parts; and

curing the coating material in which the microparticles are distributed densely in some parts and sparsely in other parts to form an optical layer,

wherein an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of a surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

8. An antiglare film comprising:

a base member; and

an antiglare layer disposed on the base member, the antiglare layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin on the base member, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the antiglare layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the antiglare layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

9. An optical layer-attached polarizer comprising:

a polarizer; and

an optical layer disposed on the polarizer, the optical layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

10. A display apparatus comprising:

a display unit configured to display images; and

an optical layer disposed at a display surface side of the display unit, the optical layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

11. A display apparatus comprising:

a display unit configured to display images;

a front member disposed at a front surface side of the display unit; and

an optical layer disposed at the front surface side of the display unit and/or a rear surface side of the front member, the optical layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.

12. A display apparatus comprising:

a display unit configured to display images;

a rear member disposed at a rear surface side of the display unit; and

an optical layer disposed at the rear surface side of the display unit and/or a front surface side of the rear member, the optical layer having an asperity in a surface,

wherein the asperity is formed by applying a coating material containing microparticles and a resin, distributing the microparticles densely in some parts and sparsely in other parts by convections that occur in the coating material, and curing the coating material,

an average diameter of the microparticles is 2.4 μm or more and 8 μm or less,

an average thickness of the optical layer is 6.4 μm or more and 18 μm or less,

an arithmetic mean roughness Ra of a roughness profile of the surface of the optical layer is 0.03 μm or more and 0.15 μm or less and a root-mean-square slope RΔq of the roughness profile is 0.01 or more and 0.03 or less, and

the difference in refractive index between the resin and the microparticles is 0 or more and 0.015 or less.