Thermoplastic film for airbag covers
View Patent ↗A thermoplastic film for airbag covers contains a cover layer and a foam layer. The cover layer is made of at least two layers, having an outer layer and an inner layer, and an elongation at tear of the inner layer of the cover layer and of the foamed layer is considerably less than the elongation at tear of the outer layer of the cover layer.
1. A thermoplastic film, comprising:
a compact cover layer having a three-dimensionally structured surface;
a foamed layer disposed on an underside of said compact cover layer, the thermoplastic film being applied in a shaping processing step to a support corresponding to a form of a component and thereby receiving its component form; and
said compact cover layer being uniformly compliant and of an at least two-ply form, containing an outer ply without weakening lines and an inner ply without weakening lines adjacent said foamed layer, said inner ply of said compact cover layer and said foamed layer having an elongation at tear being less than an elongation at tear of said outer ply of said compact cover layer.
2. The thermoplastic film according to claim 1 , wherein the elongation at tear of said inner ply on breaking in a longitudinal direction is less than or equal to 600% and in a transverse direction is less than or equal to 500% of a respective original dimension.
3. The thermoplastic film according to claim 2 , wherein the elongation at tear of said inner ply on breaking in the longitudinal direction is less than or equal to 500%, and in the transverse direction less than or equal to 400% of the respective original dimension.
4. The thermoplastic film according to claim 1 , wherein a tearing resistance of said inner ply in a longitudinal direction and in a transverse direction is 8 to 25 MPa.
5. The thermoplastic film according to claim 1 , wherein said inner and outer plies of said compact cover layer have a thickness of in each case 0.2 to 0.6 mm.
6. The thermoplastic film according to claim 1 , wherein the elongation at tear of said foamed layer on breaking in a longitudinal direction is less than or equal to 400% and in a transverse direction is less than or equal to 300% of a respective original dimension.
7. The thermoplastic film according to claim 6 , wherein the elongation at tear of said foamed layer on breaking in the longitudinal direction is less than or equal to 300%, and in the transverse direction is less than or equal to 200% of the respective original dimension.
8. The thermoplastic film according to claim 1 , wherein said foamed layer has a thickness of 0.5 to 4 mm.
9. The thermoplastic film according to claim 1 , wherein said foamed layer has a density of 40 to 300 kg/m 3 .
10. The thermoplastic film according to claim 2 , wherein the elongation at tear of said inner ply on breaking in the longitudinal direction is less than or equal to 400%, and in the transverse direction is less than or equal to 300% of the respective original dimension.
11. The thermoplastic film according to claim 1 , wherein a tearing resistance of said inner ply in a longitudinal direction and in a transverse direction is 10 to 15 MPa.
12. The thermoplastic film according to claim 1 , wherein said inner and outer plies of said compact cover layer have a thickness of in each case 0.2 to 0.4 mm.
13. The thermoplastic film according to claim 6 , wherein the elongation at tear of said foamed layer on breaking in the longitudinal direction is less than or equal to 200%, and in the transverse direction is less than or equal to 150% of the respective original dimension.
14. The thermoplastic film according to claim 1 , wherein said foamed layer has a density of 40 to 200 kg/m 3 .
15. The thermoplastic film according to claim 1 , wherein said foamed layer has a density of 40 to 200 kg/m 3 .
16. The thermoplastic film according to claim 1 , wherein the thermoplastic film is for airbag covers for interior trim of motor vehicles.
17. An interior trim part for a motor vehicle, comprising:
a thermoplastic film containing a compact cover layer having a three-dimensionally structured surface and a foamed layer disposed on an underside of said compact cover layer, said thermoplastic film being applied in a shaping processing step to a support corresponding to a form of a component and thereby receiving its component form, said compact cover layer being uniformly compliant and of an at least two-ply form at least in one of a region of airbag covers and in a region of tear-open seams of the airbag covers, said two-ply form having an outer ply without weakening lines and an inner ply without weakening lines adjacent said foamed layer, said inner ply of said compact cover layer and said foamed layer having an elongation at tear which is less than an elongation at tear of said outer ply of said cover layer.
18. The interior trim part for the motor vehicle according to claim 17 , wherein the interior trim part is a dashboard.
19. A thermoplastic film, comprising:
a compact cover layer having a three-dimensionally structured surface;
a foamed layer disposed on an underside of said compact cover layer, the thermoplastic film being applied in a shaping processing step to a support corresponding to a form of a component and thereby receiving its component form; and
said compact cover layer being uniformly compliant and of an at least two-ply form, containing an outer ply having a substantially uniform thickness and an inner ply having a substantially uniform thickness adjacent said foamed layer, said inner ply of said compact cover layer and said foamed layer having an elongation at tear being less than an elongation at tear of said outer ply of said compact cover layer.