View Patent ↗A method for reducing cure shrinkage of a thermoset resin includes forming a plurality of surface modified nanofibers. The surface modified nanofibers are formed by soaking nanofibers in an oxidizing acidic solvent. An oxidizing agent is added to the soaking nanofibers, thereby generating heat sufficient for at least one of in-situ oxidation and in-situ exfoliation of a subsurface of each of the nanofibers. Excess oxidizing agent and acidic solvent are removed from the nanofibers, which are then dried. The dried nanofibers have reduced surface hydrophobicity. The surface modified nanofibers are substantially uniformly dispersed into the thermoset resin. The surface modified nanofibers are adapted to reduce cure shrinkage of the thermoset resin during subsequent curing processes.
1. A method for making a surface modified nanofiber, the method comprising:
soaking a nanofiber in an oxidizing acidic solvent;
adding an oxidizing agent to the soaking nanofiber, thereby generating heat sufficient for at least one of in-situ oxidation and in-situ exfoliation of a subsurface of the nanofiber;
removing excess oxidizing agent and oxidizing acidic solvent from the nanofiber; and
drying the nanofiber, thereby forming the surface modified nanofiber having reduced surface hydrophobicity, the surface modified nanofiber adapted to reduce cure shrinkage of a thermoset resin into which it is incorporated.
2. The method as defined in claim 1 wherein the oxidizing agent is a transition metal in an oxidation state greater than about 3 valence states.
3. The method as defined in claim 1 wherein prior to soaking the plurality of nanofibers in the oxidizing acidic solvent and adding the oxidizing agent, the plurality of nanofibers is soaked in water.
4. The method as defined in claim 1 wherein soaking the nanofiber in the oxidizing acidic solvent is accomplished for a time ranging from about 1 minute to about 60 minutes.
5. The method as defined in claim 1 , further comprising mixing the nanofiber with a surfactant solution prior to drying the nanofiber.
6. The method as defined in claim 1 wherein the nanofiber is a carbon nanofiber.
7. The method as defined in claim 1 wherein removing excess oxidizing agent and oxidizing acidic solvent is accomplished by rinsing the soaking nanofiber having the oxidizing agent therein with water.
8. The method as defined in claim 1 , further comprising:
mixing the surface modified nanofiber in an interface polymer; and
substantially uniformly mixing the surface modified nanofiber in the thermoset resin.