Valve metal-oxide powder and method for producing said powder
View Patent ↗A process for the production of a valve metal oxide powder, in particular an Nb 2 O 5 or Ta 2 O 5 powder by continuous reaction of a fluoride-containing valve metal compound with a base in the presence of water and calcination of the resultant product, wherein the reaction is performed in just one reaction vessel and at a temperature of at least 45° C. Valve metal oxide powders obtainable in said manner which exhibit a spherical morphology, a D 50 value of 10 to 80 μm and an elevated BET surface area.
1. A spherical valve metal oxide powder with an average particle diameter D 50 , of 10 to 80 μm, characterized in that the BET surface area is at least 10 m 2 /g.
2. The valve metal oxide powder according to claim 1 , wherein the valve metal oxide is a niobium oxide or tantalum oxide.
3. The valve metal oxide powder according to claim 2 , wherein the valve metal oxide is Nb 2 O 5 or Ta 2 O 5 .
4. The valve metal oxide powder according to claim 1 , wherein the BET surface area, is at least 15 m 2 /g.
5. The valve metal oxide powder according to claim 1 , wherein the BET surface area is at least 20 m 2 /g.
6. The valve metal oxide powder according to claim 1 , wherein the BET surface area is at least 40 m 2 /g.
7. The valve metal oxide powder according to claim 1 , wherein the BET surface area is at least 60 m 2 /g.
8. The valve metal oxide powder according to claim 1 , wherein when applying said powder onto a square slide with an adhesive surface, an area is measured in which at least 200 particles are visible, and the powder particles visible in this image are evaluated by laying a circle around an imaged powder particle, the circle touching the two maximally distant points on the circumference of the particle, a further circle with an identical center point is drawn, but now touching the two minimally distant points on the circumference of the particle, the ratio of the diameter of these two circles is used as a criterion for describing the morphology of the valve metal oxide powder wherein at least 95% of the powder particles exhibit a ratio of the diameter of the larger circle to the diameter of the smaller circle of 1.0 to 1.4.
9. A process for the production of valve metal powders or valve metal suboxide powders which comprises converting the valve metal oxide powder according to claim 1 to a valve metal powder or valve metal suboxide powder by reduction.
10. The valve metal oxide powder according to claim 8 , wherein the BET surface area is at least 60 m 2 /g.
11. The valve metal oxide powder according to claim 3 , wherein the BET surface area is at least 60 m 2 /g.