Oxidation catalyst and method for destruction of CO, VOC and halogenated VOC
View Patent ↗An oxidation catalyst deposited on a substrate is described for the destruction of CO and volatile organic compounds, in particular halogenated organic compounds, from an emissions stream at temperatures from 250° C. to 450° C. The oxidation catalyst includes at least two platinum group metals, one of which is either platinum or ruthenium, supported on refractory oxides, such as a solid solution of CeO 2 and ZrO 2 , and tin oxide and/or silica.
1. An oxidation catalyst for the destruction of CO and volatile organic compounds, in particular halogenated organic compounds, from an emissions stream, wherein the oxidation catalyst comprises
at least two platinum group metals, one of which comprises ruthenium or platinum,
a refractory oxides support comprising a solid solution of CeO 2 and ZrO 2 ; and
tin oxide having a surface area from about 2 m 2 /g to 200 m 2 /g and a particle size from about 1 to 20 micrometers.
2. The oxidation catalyst of claim 1 deposited on a substrate having a honeycomb or a monolithic structure wherein the substrate is produced from the group consisting of cordierite, mullite, iron-chromium alloy and stainless steel.
3. The oxidation catalyst of claim 1 wherein the two platinum group metals comprise ruthenium and platinum.
4. The oxidation catalyst of claim 1 wherein the platinum group metals consist essentially of ruthenium and platinum.
5. The oxidation catalyst of claim 3 wherein the ratio of ruthenium to platinum is 20 to 1 to 1 to 20.
6. The oxidation catalyst of claim 1 wherein the refractory oxides support is stabilized by blending with one or more rare earth metal oxides.
7. The oxidation catalyst of claim 6 wherein the rare earth metal oxides are selected from the group consisting of lanthanum oxide, cerium oxide, yttrium oxide, praseodymium oxide, neodymium oxide, and mixtures thereof.
8. The oxidation catalyst of claim 2 wherein the platinum group metals are deposited on the substrate at a loading that comprises from about 10 to about 200 g/cf (0.35 g/L to 7.1 g/L).
9. The oxidation catalyst of claim 1 wherein the oxidation catalyst further comprises silica, which comprises from about 5% to about 50%, by weight, of the oxidation catalyst.
10. The oxidation catalyst of claim 1 wherein the oxidation catalyst further comprises silica selected from the group consisting of amorphous silica, precipitated silica, molecular sieves, MCM-41, SBA-15, and combinations thereof.
11. The oxidation catalyst of claim 1 wherein the oxidation catalyst further comprises silica comprising amorphous silica with a surface area more than about 200 m 2 /g, a pore size greater than about 100 angstrom and a particle size from about 0.5-20 micrometers.
12. The catalyst of claim 1 wherein the refractory metal oxides comprise from about 10% to about 95%, by weight of the oxidation catalyst.
13. The oxidation catalyst of claim 1 wherein the tin oxide comprises about 5% to about 50%, by weight of the oxidation catalyst.
14. A process for the production of an oxidation catalyst deposited on a substrate for the destruction of CO and volatile organic compounds, in particular halogenated organic compounds, from an emissions stream comprising
preparing an aqueous mixture slurry comprising a solid solution of CeO 2 and ZrO 2 , and one or both members selected from the group consisting of tin oxide and silica to form a mixture;
blending the mixture;
coating a substrate with the blended mixture;
drying and calcining the coated substrate;
depositing at least two platinum group metal precursor materials, comprising at least one of platinum and ruthenium, on the calcined coated substrate; and
drying and calcining the platinum group metals coated substrate.
15. The process of claim 14 wherein the aqueous mixture slurry is blended with a binder selected from the group consisting of colloidal alumina, colloidal silica, colloidal titania, colloidal zirconia, colloidal ceria and mixtures thereof.
16. A process for the production of an oxidation catalyst for the destruction of CO and volatile organic compounds, in particular halogenated organic compounds, from an emissions stream comprising
depositing at least two precious metal precursors on at least one component comprising a solid solution of CeO 2 and ZrO 2 , and one or both members selected from the group consisting of tin oxide and silica to form a mixture;
blending the mixture;
coating a substrate with the blended mixture;
drying and calcining the coated substrate.
17. A method for treating a gas stream that contains CO and VOCs, including halogenated VOCs, and mixtures thereof, the method comprising
combining a gas stream that contains CO and VOCs, including halogenated VOCs, with oxygen; and
contacting the combined oxygen-gas stream with the catalyst of claim 1 at a temperature from about 200° C. to 500° C.
18. The method of claim 17 wherein the gas stream comprises at least one halogenated organic compound.
19. The method of claim 17 wherein the gas stream comprises a brominated organic compound.
20. An oxidation catalyst for the destruction of CO and volatile organic compounds, in particular halogenated organic compounds, from an emissions stream, wherein the oxidation catalyst comprises
at least two platinum group metals, comprising ruthenium and platinum, wherein the ratio of ruthenium to platinum is 20 to 1 to 1 to 20,
a refractory oxides support comprising a solid solution of CeO 2 and ZrO 2 ; and
one or both members selected from the group consisting of silica and tin oxide.