View Patent ↗One aspect of the present invention includes a swellable sol-gel composition including a plurality of interconnected organosilica nanoparticles. Another aspect of the present invention includes a swellable composite including a plurality of interconnected organosilica nanoparticles and a particulate material capable of binding to or reacting with a non-polar or organic sorbate. When dried, the sol-gel composition and the swellable composite may be capable of swelling to at least twice their dried volume when placed in contact with a non-polar or organic sorbate.
1. A composite material comprising an aromatically-bridged, organosiloxane sol-gel composition containing a plurality of alkylsiloxy substituents and a non-polar or organic sorbate-reactive particulate material.
2. The composite material of claim 1 wherein the aromatically bridged, organosiloxane sol-gel composition is derived from a trialkoxysilane corresponding to the formula:
(alkoxy) 3 Si—(CH 2 ) n —Ar—(CH 2 ) m —Si(alkoxy) 3
where n and m are individually an integer from 1 to 8, Ar is a single-, fused-, or poly-aromatic ring, and each alkoxy is independently a C 1 to C 5 alkoxy.
3. The composite material of claim 2 wherein n and m are individually an integer from 1 to 3, Ar is a phenyl, biphenyl or naphthyl ring and each alkoxy is independently a C 1 to C 3 alkoxy.
4. The composite material of claim 3 wherein the trialkoxysilane is a bis(trialkoxysilylalkyl)benzene.
5. The composite material of claim 4 wherein the bis(trialkoxysilylalkyl)benzene is 1,4-bis(trimethoxysilylmethyl)benzene or bis(trimethoxysilylethyll)benzene.
6. The composite material of claim 2 wherein the alkylsiloxy substituents correspond to the formula:
—O x —S 1 —Ry
where R is independently a hydrocarbon containing up to about 30 carbons, x is 1 or 2, y is 2 or 3 and the total of x and y is 4.
7. The composite material of claim 6 wherein R is a straight-chain hydrocarbon, a branched-chain hydrocarbon, a cyclic hydrocarbon or an aromatic hydrocarbon.
8. The composite material of claim 6 wherein the alklysiloxy substituents include at least one heteroatom selected from sulfur, oxygen, nitrogen, phosphorous, a halogen or combinations thereof.
9. The composite material of claim 2 wherein the non-polar or organic sorbate-reactive particulate material is a reactive metal capable of reducing organic sorbates.
10. The composite material of claim 9 wherein the non-polar or organic reactive particulate material is a transition metal capable of reducing organic sorbates.
11. The composite material of claim 10 wherein the transition metal is ZVI, copper, nickel, cobalt, silver, gold, palladium, zinc or platinum.
12. The composite material of claim 10 wherein the transition metal is ZVI present in an amount of from about 0.5% to about 5%, by weight of dried sol-gel composition.
13. The composite material of claim 2 wherein the sorbate-reactive particulate material is a catalyst.
14. The composite material of claim 13 wherein the non-polar or organic sorbate-reactive particulate material includes a metal catalyst coating.
15. The composite material of claim 14 wherein the metal catalyst coating is a transition metal coating.
16. The composite material of claim 15 , wherein the transition metal coating is a palladium, nickel or zinc coating.
17. The composite material of claim 13 wherein the particulate material catalyzes the dehalogenation of a halogenated organic sorbate.
18. The composite material of claim 17 wherein the halogenated organic sorbate is PCE, CT, TCE, TCM, cDCE, TBM, tDCE, 12EDB, 11DCE, Freon 113, VC, Freon 11, HCA, 1122TeCA, 123TCP, 1112TeCA, 12DCP, 111TCA, lindane, 112TCA, HCBD, 11DCA, or a polychlorinated biphenyl having the formula C 12 H 10-x Cl x where x is an integer>1 and <11.
19. The composite material of claim 2 wherein the non-polar or organic sorbate-reactive particulate material is a reducing agent.