Cubic boron nitride ceramic composites and methods of making thereof
View Patent ↗Composite materials composed of cubic boron nitride (cBN) and a matrix component of various ceramic oxides, nitrides, and solid solutions of matrix materials as well as whisker reinforcements. Methods of manufacture and their use in high performance machining of ferrous metals are also claimed and disclosed.
1. An as-sintered ceramic matrix composite comprising:
between about 10 wt % to about 20 wt % cBN;
between about 40 wt % to about 80 wt % aluminum oxide;
and between about 10 wt % to about 50 wt % silicon nitride.
2. The ceramic matrix composite according to claim 1 , further comprising aluminum nitride.
3. The ceramic matrix composite according to claim 1 , further comprising solid solutions of silicon nitride and aluminum oxide.
4. The ceramic matrix composite according to claim 1 , further comprising a solid solution of silicon aluminum oxynitride.
5. The ceramic matrix composite according to claim 2 , further comprising a solid solution of silicon aluminum oxynitride.
6. The ceramic matrix composite according to claim 2 , further comprising solid solutions of silicon nitride, aluminum oxide and aluminum nitride.
7. The ceramic matrix composite according to claim 1 , further comprising oxides of lanthanoids, yttrium or scandium.
8. The ceramic matrix composite according to claim 1 , where said composite further comprises up to about 15 wt % ceramic whiskers.
9. The ceramic matrix composite according to claim 8 , further comprising about 5 wt % or less of an additive selected from oxides of lanthanoids, yttrium or scandium.
10. An as-sintered ceramic matrix composite comprising:
between about 10 wt % to about 20 wt % cubic boron nitride (cBN);
between about 40 wt % to about 80 wt % aluminum oxide;
between about 10 wt % to about 50 wt % silicon nitride; and
about 5 wt % or less of an additive selected from oxides of lanthanoids, yttrium or scandium.
11. An as-sintered ceramic matrix composite comprising between about 10 wt % to about 20 wt % cubic boron nitride (cBN); between about 40 wt % to about 80 wt % aluminum oxide; between about 10 wt % to about 50 wt % silicon nitride; between about 5 wt % or less of an additive selected from oxides of lanthanoids, yttrium or scandium made from a method comprising the steps of:
providing a powder, wherein the powder comprises cBN, silicon nitride and aluminum oxide;
blending powder to form a mixture; and
sintering the mixture at a temperature of about at least 1200° C. and pressure of at least 40 kbar to form a sintered product.
12. A tool made from a method comprising the steps of:
providing a powder, wherein the powder comprises cBN, silicon nitride and aluminum oxide;
blending powder to form a mixture; and
sintering the mixture at a temperature of about at least 1200° C. and pressure of at least 40 kbar to form a sintered product; wherein the tool comprises:
between about 10 wt % to about 20 wt % cubic boron nitride (cBN); between about 40 wt % to about 80 wt % aluminum oxide; between about 10 wt % to about 50 wt % silicon nitride; between about 5 wt % or less of an additive selected from oxides of lanthanoids, yttrium or scandium.