Flexible, High Temperature Rated LLDPE Jacket Composition
Polymer compositions composed of a polyethylene resin (e.g., LLDPE), carbon black and an olefin block interpolymer are provided, which are useful for, among other things, the production of wire and cable jacketing that possess an increased high temperature rating, flexibility and comparable ease of removal of the jacket from the cable core.
1 . A polymer composition, comprising:
70-90% by weight LLDPE resin;
1-20% by weight olefin block interpolymer;
1-15% by weight carbon black; and
0.1-0.5% by weight antioxidant;
the % by weight based on the total weight of the composition; and
the polymer composition having a heat deformation of less than 30% at 121° C. (as measured by ASTM D-4565) and a flexural modulus below 30,000 psi (206.90 MPa) (as measured by ASTM D-790).
2 . The polymer composition of claim 1 , wherein the flexural modulus is 20% to 50% less than the polymer composition having 0% by weight of olefin block interpolymer.
3 . The polymer composition of claim 1 , having a heat deformation as measured by ASTM D-4565 (121° C.) of less than 30% and suitable for use in a 105° C.-rated cable jacket.
4 . A polymer composition, comprising:
70-90% by weight polyethylene resin; and
1-20% by weight ethylene/α-olefin block polymer having a melt index (I 2 ) less than 15 g/10 minutes as measured by ASTM D-1238 (190° C./2.16 kg) and a density less than 0.900 g/cm 3 (ASTM D-792);
the polymer composition having a higher temperature rating and a lower flexural modulus than the polymer composition without the olefin block interpolymer; the % by weight based on the total weight of the composition.
5 . The polymer composition of claim 4 , further comprising 1-5% by weight carbon black.
6 . The polymer composition of claim 4 , wherein the polyethylene resin is a linear low density polyethylene (LLDPE).
7 . The polymer composition of claim 6 , wherein the density of the LLDPE is 0.910-0.925 g/cm 3 , as measured by ASTM D-792.
8 . The polymer composition of claim 6 , wherein the composition density is 0.925 to 0.931 g/cm 3 , as measured by ASTM D-792.
9 . The polymer composition of claim 4 , wherein the polyethylene resin is prepared with a Ziegler-Natta catalyst.
10 . The polymer composition of claim 4 , wherein the polyethylene resin is prepared using a metallocene catalyst.
11 . The polymer composition of claim 11 , wherein the metallocene catalyst is a constrained geometry catalyst (CGC).
12 . The polymer composition of claim 4 , wherein the polyethylene resin is a low density polyethylene (LDPE).
13 . The polymer composition of claim 13 , wherein the high temperature rating of the polymer composition is greater than 70° C., as measured by heat deformation according to ASTM D-4565 (at 100° C.).
14 . The polymer composition of claim 4 , wherein the polyethylene resin is a high density polyethylene (HDPE).
15 . The polymer composition of claim 4 , wherein the polyethylene resin is a medium density polyethylene (MDPE).
16 . The polymer composition of claim 5 , wherein the polymer composition has a flexural modulus of 20 to 70% less than the polymer composition without the olefin block interpolymer.
17 . The polymer composition of claim 5 , wherein the polymer composition has a heat deformation at 121° C. of less than 30%.
18 . A flexible and high temperature rated cable jacket material comprising the composition of claim 1 .
19 . A cable, comprising a flexible outer sheath comprising the composition of claim 1 , the sheath having a flexural modulus below 30,000 psi (206.9 MPa) as measured by ASTM D-790, and a heat deformation of less than 30% (at 121° C.) as measured by ASTM D-4565.