Photopolymer formulations having a low crosslinking density

1. A photopolymer formulation comprising a three-dimensionally crosslinked organic polymer A) or the precursors thereof as a matrix, a compound B) comprising groups that react with ethylenically unsaturated compounds via polymerization under the action of actinic radiation and is present in solution or dispersion in said matrix, and C) at least one photoinitiator, wherein the network density of said three-dimensionally crosslinked organic polymer, expressed as the average molecular weight M C of the segments bridging two polymer strands, is at least 2685 g/mol, wherein the ratio Q of the molecular weight M C to the number average molecular weight M Mo of B) is greater than 3.30, wherein a cured composition prepared from the photopolymer formulation has a plateau modulus G 0 of greater than 0.05 MPa and less than 1.0 MPa, wherein the plateau modulus G 0 is determined by measuring the curing of the matrix in an oscillation rheometer as follows:

plate spacing 250 μm,

oscillation measuring mode at a constant angular frequency ω 0 of 10 rad/s and a controlled logarithmic deformation amplitude ramp of 1%

temperature 50° C., normal force regulation set at 0 Newton

recording of the storage modulus G′ over the measuring time for at least 2 hours or until a constant value of G max of G′ was reached; this value is referred to as G 0 .

2. The photopolymer formulation of claim 1 , wherein the network density of said three-dimensionally crosslinked organic polymer is in the range of from 7500 to 55000 g/mol.

3. The photopolymer formulation of claim 1 , wherein the ratio Q is greater than 10.00.

4. The photopolymer formulation of claim 1 , wherein said three-dimensionally crosslinked organic polymers comprise urethane groups.

5. The photopolymer formulation of claim 1 , wherein said three-dimensionally crosslinked organic polymers are composed of an isocyanate component a) and an isocyanate-reactive component b).

6. The photopolymer formulation of claim 1 , wherein A) comprises an isocyanate component a) and an isocyanate-reactive component b).

7. The photopolymer formulation of claim 6 , wherein component a) comprises a polyisocyanate based on HDI with isocyanurate and/or iminooxadiazinedione structures or a prepolymer having an NCO functionality of from 2 to 5 with allophanate and/or urethane structures based on HDI and/or TMDI and a polyether polyol, polyester polyol, and/or polycarbonate polyol.

8. The photopolymer formulation of claim 7 , wherein the polyisocyanates has a residual contents of free monomeric isocyanate of less than 1% by weight.

9. The photopolymer formulation of claim 6 , wherein component b) comprises a polypropylene oxide, a polyethylene oxide, and/or combinations thereof in the form of a random or block copolymer and/or a block copolymer of the abovementioned type which additionally comprises tetrahydrofuran, butylene oxide, ors caprolactone as monomer units, wherein the OH functionality is from 1.5 to 6 and the number average molecular weight is from 200 to 18000 g/mol.

10. The photopolymer formulation of claim 1 , wherein said compound of B) has a refractive index n D 20 of greater than 1.54.

11. The photopolymer formulation of claim 1 , wherein said compound of B) comprise acrylate and/or methacrylate groups as radiation-curing groups.

12. A medium suitable for recording visual holograms produced from the photopolymer formulation of claim 1 .

13. An optical element, image, or representation produced from the medium of claim 12 .

14. A method for exposing the medium of claim 12 comprising selectively polymerizing writing monomers with actinic radiation.

15. A method for preparing a photopolymer formulation comprising mixing a three-dimensionally crosslinked organic polymer A) or the precursors thereof as a matrix, a compound B) comprising groups that react with ethylenically unsaturated compounds via polymerization under the action of actinic radiation and is present in solution or dispersion in said matrix, and C) at least one photoinitiator, and optionally catalysts, free radical stabilizers, solvents, additives and other auxiliaries and/or additives,

wherein the components chosen for the photopolymer formulation are only compounds wherein the network density of said three-dimensionally crosslinked organic polymer, expressed as the average molecular weight M C of the segments bridging two polymer strands, is at least 2685 g/mol, wherein the ratio Q of the molecular weight M C to the number average molecular weight M Mo of B) is greater than 3.30, and determining a plateau modulus G 0 by measuring the curing of the matrix in an oscillation rheometer as follows:

plate spacing 250 μm,

oscillation measuring mode at a constant angular frequency ω 0 of 10 rad/s and a controlled logarithmic deformation amplitude ramp of 1%

temperature 50° C., normal force regulation set at 0 Newton

recording of the storage modulus G′ over the measuring time for at least 2 hours or until a constant value of G max of G′ was reached; this value is referred to as G 0 ,

wherein the cured composition prepared from the photopolymer formulation has a plateau modulus G 0 of greater than 0.05 MPa and less than 1.0 MPa.