Method of making solar cell contacts
View Patent ↗Formulations and methods of making solar cells are disclosed. In general, the invention presents a solar cell contact made from a mixture wherein the mixture comprises a solids portion and an organics portion, wherein the solids portion comprises from about 85 to about 99 wt % of silver, and from about 1 to about 15 wt % of a glass component wherein the glass component comprises from about 15 to about 75 mol % PbO, and from about 5 to about 50 mol % SiO 2 , and preferably with no B 2 O 3 .
1. A composition for forming a solar cell contact, the composition comprising:
an organic portion; and
a solids portion comprising:
from about 85% to about 99% by weight of a conductive metal component consisting of a silver component; and
from about 1% to about 15% by weight of a glass component wherein the glass component consists of 15 mol % to 75 mol % PbO, 5 mol % to 50 mol % SiO 2 , about 0.1 mol % to about 15 mol % Al 2 O 3 , about 0.1 mol % to about 8 mol % P 2 O 5 , optionally about 0.1 mol % to about 10 mol % Ta 2 O 5 , and optionally about 0.1 mol % to about 10 mol % ZrO 2 , and is free of B 2 O 3 .
2. The composition of claim 1 wherein the weight ratio of the solids portion to the organics portion is from about 20:1 to about 1:20.
3. The composition of claim 2 wherein the solids portion comprises a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , B 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof.
4. The composition of claim 2 wherein the solids portion comprises from about 60 weight % to about 95 weight % of flaked silver or powdered silver, and from about 0.1 weight % to about 20 weight % of colloidal silver, based upon 100% total weight of the solids portion.
5. The composition of claim 2 wherein the silver component comprises silver selected from the group consisting of flakes, powder, colloidal particles of silver and combinations thereof, wherein the solids portion further comprises phosphorus, at least a portion of which is present as a coating on at least a portion of the selected silver flakes, powder colloidal particles, and combinations thereof.
6. The composition of claim 2 wherein the solids portion comprises a crystalline additive selected from the group consisting of Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , B 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof.
7. The composition of claim 1 wherein the glass component further includes from about 1 mol % to about 30 mol % Bi 2 O 3 .
8. The composition of claim 1 wherein the glass component includes from about 0.1 mol % to about 10 mol % Ta 2 O 5 .
9. The composition of claim 8 wherein the glass component includes from about 0.1 mol % to about 10 mol % ZrO 2 .
10. The composition of claim 1 wherein the glass component further includes from about 0.1 mol % to about 15 mol % HfO 2 +In 2 O 3 +Ga 2 O 3 .
11. The composition of claim 1 wherein the silver component contains a compound selected from the group consisting of an oxide of silver, a salt of silver, and combinations thereof.
12. The composition of claim 1 wherein the solids portion consists of:
the conductive metal component;
the glass component;
optionally a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof;
optionally phosphorus component, silicon, carbon powder, or combinations thereof; and
optionally a low melting metal additive selected from the group consisting of Pb, Bi, Zn, In, Ga, and Sb and alloys of the at least one metal with at least one other metal.
13. The composition of claim 12 wherein the phosphorous component comprises P 2 O 5 .
14. The composition of claim 1 wherein the silver component contains a salt of silver.
15. The composition of claim 1 wherein the solids portion consists of:
the conductive metal component;
the glass component; and
a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof.
16. The composition of claim 1 wherein the solids portion consists of:
the conductive metal component; and
the glass component.
17. The composition of claim 1 wherein at least portion of the metal conductive component is silver oxide and the silver oxide is dissolved in the glass component.
18. A composition comprising:
a solids portion; and
an organics portion;
wherein the solids portion comprises:
i. from about 85 to about 99 weight % of a conductive metal component consisting of silver, and
ii. from about 1 to about 15 weight % of glass component,
iii. wherein the glass component comprises:
a. from about 58 to about 70 mol % PbO,
b. from about 20 to about 31 mol % SiO 2 , and
c. about 1 to about 11 mol % Al 2 O 3 , and
d. optionally about 0.1 to about 10 mol % Ta 2 O 5
e. optionally about 0.1 to about 10 mol % ZrO 2 ,
f. about 0.1 mol % to about 8 mol % P 2 O 5 , and
g. no B 2 O 3 .
19. The composition of claim 18 wherein the weight ratio of the solids portion to the organics portion is from about 20:1 to about 1:20.
20. The composition of claim 18 wherein the glass component comprises about 0.1 to about 10 mol % Ta 2 O 5 .
21. The composition of claim 20 wherein the glass component comprises about 0.1 to about 10 mol % ZrO 2 .
22. The composition of claim 18 wherein the glass component further comprises about 0.1 to about 15 mol % HfO 2 +In 2 O 3 +Ga 2 O 3 .
23. The composition of claim 18 wherein the solids portion further comprises a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof.
24. The composition of claim 18 wherein the solids portion comprises about 60 to about 95 weight % of flaked silver or powdered silver, and about 0.1 to about 20 weight % of colloidal silver.
25. The composition of claim 18 wherein the silver is in a form selected from the group consisting of flakes, powder, colloidal particles of silver, and combinations thereof, and wherein the solids portion further comprises phosphorus, at least a portion of which is present as a coating on at least a portion of the silver flakes, powder or colloidal particles, or combinations thereof.
26. The composition of claim 18 wherein the silver component contains a compound selected from the group consisting of an oxide of silver, a salt of silver, and combinations thereof.
27. The composition of claim 18 wherein the solids portion further comprises at least one metal selected from the group consisting of Pb, Bi, Zn, In, Ga, and Sb and alloys of the at least one metal with at least one other metal.
28. The composition of claim 27 wherein the at least one metal is zinc.
29. The composition of claim 18 wherein the solids portion consists of:
the conductive metal component;
the glass component;
optionally a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof;
optionally phosphorus component, silicon, carbon powder, or combinations thereof; and
optionally a low melting metal additive selected from the group consisting of Pb, Bi, Zn, In, Ga, and Sb and alloys of the at least one metal with at least one other metal.
30. A composition comprising:
an organics portion; and
a solids portion, wherein the solids portion comprises
i. from about 85 to about 99 wt % of a conductive metal component consisting of a silver component, and
ii. from about 1 to about 15 wt % of a glass component
iii. wherein the glass component comprises
a. from about 58 to about 70 mol % PbO,
b. from about 20 to about 31 mol % SiO 2 ,
c. at least 1 mol % Bi 2 O 3 ,
d. about 0.1 to about 15 mol % Al 2 O 3 ,
e. optionally about 0.1 to about 10 mol % Ta 2 O 5 ,
f. optionally about 0.1 to about 10 mol % ZrO 2 ,
g. about 0.1 mol % to about 8 mol % P 2 O 5 ,and
h. no B 2 O 3 .
31. The composition of claim 30 , wherein the solids portion further comprises about 0.1 to about 10 mol % Ta 2 O 5 .
32. The composition of claim 30 wherein the solids portion consists of:
the conductive metal component;
the glass component;
optionally a crystalline additive selected from the group consisting of Bi 2 O 3 , Sb 2 O 3 , In 2 O 3 , Ga 2 O 3 , SnO, ZnO, Pb 3 O 4 , PbO, SiO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , 4PbO.SiO 2 , 3PbO.SiO 2 , 2PbO.SiO 2 , 3PbO.2SiO 2 , PbO.SiO 2 , ZnO.SiO 2 , and ZrO 2 .SiO 2 , and reaction products thereof and combinations thereof;
optionally phosphorus component, silicon, carbon powder, or combinations thereof; and
optionally a low melting metal additive selected from the group consisting of Pb, Bi, Zn, In, Ga, and Sb and alloys of the at least one metal with at least one other metal.
33. A composition for forming a solar cell contact, the composition comprising:
an organic portion; and
a solids portion comprising:
from about 85% to about 99% by weight of a conductive metal component consisting of silver powder and colloidal silver; and
from about 1% to about 15% by weight of a glass component wherein the glass component consists of 15 mol % to 75 mol % PbO, 5 mol % to 50 mol % SiO 2 , about 0.1 mol % to about 15 mol % Al 2 O 3 , about 0.1 mol % to about 8 mol % P 2 O 5 , optionally about 0.1 mol % to about 10 mol % Ta 2 O 5 , and about 0.1 mol % to about 10 mol % ZrO 2 , and is free of B 2 O 3 .