Method of deposition of metallic coatings using atomized spray
View Patent ↗A method of coating a metal substrate such as the components in second and third stages of gas turbine engines in order to increase the oxidation and corrosion resistance of the metal substrate under high temperature operating conditions, the method including the steps of forming a powdered mixture of a high-melt superalloy or MCrAlY component, where M comprises Fe, Ni and/or Co, and a low-melt component containing about 2-5 wt. % silicon, boron or hafnium, applying the powdered mixture to the surface of the metal substrate at room temperature using an atomized spray to form a uniform surface coating, and then heating the coated substrate surface under vacuum conditions to a temperature in the range of about 1900° F. to 2275° F. to obtain a uniform coating composition providing oxidation resistance to the underlying substrate.
1. A method of coating a metal substrate on a gas turbine engine in order to increase the oxidation resistance of said substrate at high temperature, comprising the steps of:
forming a powdered mixture of a high-melt superalloy component or MCrAlY, where M comprises Fe, Ni and/or Co, a lower-melting component containing a melting point depressant, said melting point depressant comprising silicon, boron, hafnium or gold, and a binder material for said powdered mixture;
applying said powdered mixture to a surface of said metal substrate at room temperature using an atomized spray to form a coating of substantially uniform thickness on said substrate surface; and
heating said coated substrate surface under vacuum conditions to a temperature in the range of about 1900° F. to 2275° F., said temperature and vacuum conditions being sufficient to liquefy said lower-melting component and remove said binder material and form a liquid phase in which the higher melting powders become suspended in said liquid phase and develop a metallurgical bond to said substrate by liquid phase sintering.
2. The method according to claim 1 , wherein said step of heating said coated substrate surface occurs in stages such that the surface temperature is raised and lowered from a temperature of about 840° F. to about 2225° F. and back down to about 1975° F.
3. The method according to claim 2 , wherein said step of heating said coated substrate surface in stages occurs over a period of about four to six hours.
4. The method according to claim 2 , wherein said step of heating said coated substrate surface in stages occurs under vacuum conditions of about 5×10 −4 torr.
5. The method according to claim 2 , wherein said step of heating said coated substrate surface under vacuum conditions achieves a level of porosity in the final heat-treated and coated surface of less than about 20%.
6. The method according to claim 1 , wherein said lower-melting component comprises silicon in an amount of about 2-12 wt. %.
7. The method according to claim 1 , wherein the amount of said high-melt component ranges from about 10% to about 60% by weight of said coating.
8. The method according to claim 1 , wherein the amount of said low-melt component ranges from about 40% to about 90%.
9. A method according to claim 1 , further comprising the step of mechanically finishing said coating on said metal substrate following said heating step.
10. The method according to claim 1 , further comprising the step of increasing the surface temperature of said coating from about 1975° F. to about 2050° F.
11. The method according to claim 1 , wherein said step of applying said powdered mixture covers only a portion of said metal substrate.
12. A method according to claim 1 , further comprising the step of reducing the temperature by 15-20° F. following an initial heat treatment, the reduced temperature being sufficient to diffuse and homogenize the final coating composition applied to said substrate.
13. A method according to claim 1 , wherein said powdered mixture comprises 50% by weight of Ni-8Cr-10Al and 50% Ni-12Cr-2Al-4Si.
14. A method according to claim 1 , wherein step of heating said coated substrate surface under vacuum conditions occurs at a pressure maintained below 5×10 −4 torr and a constant heating rate of 15-25° F. per minute.