Mixed metal hydroxides comprising amorphous aluminum hydroxide, and their preparation and use
View Patent ↗The present invention relates to a particulate mixed metal hydroxide that includes nickel, cobalt and aluminium. The powder particles have a core of nickel/cobalt hydroxide, and a surface that is coated with amorphous aluminium hydroxide. A process for the continuous preparation of such mixed metal hydroxides is also described. The process includes precipitating aluminium hydroxide in the presence of a nickel/cobalt mixed hydroxide in a tube reactor. The mixed metal hydroxides of the present invention may be used to prepare active materials for positive electrodes of a secondary battery.
1. Metal hydroxide powder particles comprising metal hydroxide particles having a core comprising nickel/cobalt hydroxide and a surface being coated with amorphous aluminium hydroxide,
in which the Ni content is 50 to 93 mol %, the Co content is 5 to 30 mol % and the Al content is 2 to 20 mol %, where the mole percents in each case are based on the total moles of Ni, Co and Al, and
a tap density of the metal hydroxide powder particles is more than 1.8 g/cm 3 .
2. Metal hydroxide powder particles according to claim 1 , wherein the tap density of the metal hydroxide powder particles is more than 2.0 g/cm 3 .