Polyethylene pipe fitting resins
View Patent ↗A polyethylene resin suitable for formation into pipes or pipe fittings is disclosed, having an MI5 of from 0.40 to 0.70 g/10 min, and comprising from 47 to 52 wt % of a low molecular weight polyethylene fraction, and from 48 to 53 wt % of a high molecular weight polyethylene fraction, wherein the high molecular weight polyethylene fraction comprises a copolymer of ethylene and 1-hexen or 1-octene.
1. Pipe fitting made from a polyethylene resin having an MI 5 of from 0.40 to 0.70 g/10 min, and comprising from 47 to 52 wt % of a low molecular weight polyethylene fraction, and from 48 to 53 wt % of a high molecular weight polyethylene fraction, wherein the high molecular weight polyethylene fraction comprises a copolymer of ethylene and either 1-hexene or 1-octene.
2. Pipe fitting according to claim 1 , wherein the low molecular weight polyethylene fraction comprises a polyethylene having a density of at least 0.965 g/cm 3 and an MI 2 of from 5 to 1000 g/10 min, and the high molecular weight polyethylene fraction has a density of from 0.910 to 0.940g/cm 3 and an MI 5 of from 0.01 to 2 g/10 min.
3. Pipe fitting according to claim 1 , characterized in that the polyethylene resin comprises 48-51% by weight with respect to the total weight of the composition of the ethylene polymer fraction (A).
4. Pipe fitting according to claim 1 , characterized in that the polyethylene resin comprises 49-51% by weight with respect to the total weight of the composition of the ethylene polymer fraction (A).
5. Pipe fitting according to claim 1 , characterized in that the polyethylene resin has a density after granulation and addition of additives of between 957 kg/m 3 and 963 kg/m 3 .
6. Pipe fitting according to claim 1 , characterized in that the polyethylene resin has an MI 5 of from 0.45 to 0.65 g/10 min, preferably 0.50 to 0.60 g/10 min.
7. Pipe fitting according to claim 1 , characterized in that the polyethylene resin has a density after granulation and addition of additives between 959 kg/m 3 and 961 kg/m 3 , or a natural density of between 950 and 952 kg/m 3 .
8. Pipe fitting according to claim 1 , characterized in that the polyethylene resin comprises at least 0.2% mole % and at most 0.7 mole % of monomer units derived from 1-hexene or 1-octene.
9. Pipe fitting made from a polyethylene resin having an MI 5 of from 0.40 to 0.70 g/10 min, a density after granulation and addition of additives between 957 kg/m 3 and 963 kg/m 3 , and a stress crack resistance time of at least 165 hours at 80° C. and 5.5 MPa according to standards EN1555-EN12201-ISO4427-ISO4437.
10. Pipe fitting according to claim 9 , wherein the polyethylene resin comprises from 47 to 52 wt % of a low molecular weight polyethylene fraction, and from 48 to 53 wt % of a high molecular weight polyethylene fraction, wherein the low molecular weight polyethylene fraction comprises a polyethylene having a density of at least 0.965 g/cm 3 and an MI 2 of from 5 to 1000 g/10 min, and the high molecular weight polyethylene fraction has a density of from 0.910 to 0.940g/cm 3 and an MI 5 of from 0.01 to 2 g/10 min.
11. Pipe fitting according to claim 9 , characterized in that the polyethylene resin has an MI 5 of from 0.45 to 0.65 g/10 min, preferably 0.50 to 0.60 g/10 min.
12. Pipe fitting according to claim 9 , characterized in that the polyethylene resin has a density after granulation and addition of additives between 959 kg/m 3 and 961 kg/m 3 , or a natural density of between 950 and 952 kg/m 3 .
13. Pipe fitting according to claim 9 , characterized in that the polyethylene resin comprises at least 0.2% mole % and at most 0.7 mole % of monomer units derived from 1-hexene or 1-octene.