Submicron-scale graphitic fibrils, methods for producing same and compositions containing same
View Patent ↗The present invention provides a submicron-scaled graphitic fibril having a diameter or thickness less than 1 μm, wherein the fibril is free of continuous thermal carbon overcoat, free of continuous hollow core, and free of catalyst. The fibril is obtained by splitting a micron-scaled carbon fiber or graphite fiber along the fiber axis direction. The diameter or thickness is preferably less than 500 nm and can be greater or less than 100 nm. These graphitic fibrils exhibit exceptionally high electrical conductivity, thermal conductivity, elastic modulus, and strength. The present invention also provides several products that contain submicron graphitic fibrils: (a) paper, thin-film, mat, and web products; (b) rubber or tire products; (c) energy conversion or storage devices, such as fuel cells, lithium-ion batteries, and supercapacitors; (d) adhesives, inks, coatings, paints, lubricants, and grease products; (e) heavy metal ion scavenger; (f) absorbent (e.g., to recover spill oil); (g) sensors; (h) friction and brake components; (i) radiation-shield components; and (j) nanocomposite materials.
1. A submicron-scaled graphitic fibril having a thickness in the range from 100 nm to 1 μm and a length greater than 5 μm, wherein throughout the fibril, said fibril is free of continuous thermal carbon overcoat, free of continuous hollow core, and free of catalyst, and wherein said fibril comprises at least 95% by weight carbon atoms arranged in a hexagon or graphene structure that form a graphite single crystal, and said fibril is obtained by splitting a micron-diameter carbon fiber or graphite fiber.
2. The graphitic fibril of claim 1 wherein said diameter or thickness is in the range from 500 run to 1 μm.
3. The graphitic fibril of claim 1 wherein said diameter or thickness is between 100 and 500 μm.
4. The graphitic fibril of claim 1 wherein said fibril has a length greater than 10 μm.
5. The graphitic fibril of claim 1 wherein said fibril is obtained by thermo-chemically splitting a carbon or graphite fiber into an aggregate of multiple interconnected or partially bonded fibrils and separating said graphitic fibril from said aggregate.
6. The graphitic fibril of claim 1 wherein said fibril comprises at least 98% by weight carbon atoms arranged in a hexagon or graphene structure.
7. The graphitic fibril of claim 1 wherein said fibril has an elongate axis and comprises a graphite single crystal having multiple layers of graphene plane parallel to the fibril elongate axis.
8. The graphitic fibril of claim 1 wherein said fibril comprises at least 300 layers of graphene plane.
9. The graphitic fibril of claim 1 which is prepared from a micron-diameter carbon fiber or graphite fiber having a diameter greater than or equal to 6 μm.
10. The submicron graphitic fibril of claim 1 which is prepared by using a method comprising (a) intercalating a carbon fiber or graphite fiber with an intercalating agent to form an intercalated fiber; (b) thermally and/or chemically splitting or exfoliating said intercalated fiber to obtain a split fiber; and (c) mechanically separating said graphitic fibril from said split fiber.
11. The submicron graphitic fibril of claim 1 which is prepared by using a method comprising (a) intercalating a carbon fiber or graphite fiber with a supercritical fluid to form a tentatively intercalated fiber at a first temperature and a first pressure; (b) exposing said tentatively intercalated fiber to a second temperature or a second pressure to obtain a split carbon or graphite fiber; and (c) mechanically isolating said graphitic fibril from said split fiber.
12. A nanocomposite material comprising multiple graphitic fibrils as defined in claim 1 wherein said fibrils are dispersed in a matrix material and wherein said graphitic fibrils have a weight fraction between 0.1% and 90% of the nanocomposite.
13. The nanocomposite of claim 12 wherein said matrix material is selected from the group consisting of a polymer, rubber, plastic, resin, glass, ceramic, carbon, metal, organic, and combinations thereof.