Perpendicular magnetic recording medium and method of manufacturing the same
View Patent ↗A vertical magnetic recording disc ( 100 ) includes a base ( 10 ), a magnetic recording layer ( 22 ), and a medium protection layer ( 26 ). The magnetic recording layer ( 22 ) is a ferromagnetic layer having a granular structure where a granular portion is formed. The medium protection layer ( 26 ) contains nitrogen (N) atoms and carbon (C) atoms with a number ratio (N/C) in a range from 0.050 to 0.150. In a Raman spectrum obtained by exciting the medium protection layer ( 26 ) by argon ion laser light of wavelength 514.5 nm, from which a fluorescence is removed, the peak ratio Dh/Gh is in a range from 0.70 to 0.95, when a D peak Dh appearing in the vicinity of 1350 cm −1 is separated from G peak Gh appearing in the vicinity of 1520 cm −1 by the Gauss function.
1. A perpendicular magnetic recording medium comprising:
a substrate;
a magnetic recording layer on said substrate, and a medium-protecting layer on the magnetic recording layer, wherein the magnetic recording layer is a ferromagnetic layer of a granular structure having grain boundaries formed by a non-magnetic material among crystalline particles grown in a columnar shape and containing at least cobalt (Co);
the medium protecting layer has a thickness in the range between 1.0 nm and less than 3.0 nm; and
the medium-protecting layer is composed of a coating that includes carbon as a main component and nitrogen contained in a surface layer at a number ratio (N/C) of nitrogen (N) atoms and carbon (C) atoms of 0.090 to 0.150, and in a spectrum removed fluorescence from a Raman spectrum in wavenumbers of 900 to 1800 cm −1 obtained by exciting the medium-protecting layer with argon ion laser light having a 514.5 nm wavelength, a peak ratio Dh/Gh when a D peak Dh appearing near 1350 cm −1 and a G peak Gh appearing near 1520 cm −1 are waveform-separated by a Gaussian function is no less than 0.075 to less than 0.95.
2. A perpendicular magnetic recording medium comprising:
a substrate;
a magnetic recording layer on the substrate, and
a medium-protecting layer on the magnetic recording layer, wherein
the magnetic recording layer is a ferromagnetic layer of a granular structure having grain boundaries formed by a non-magnetic material among crystalline particles grown in a columnar shape and containing at least cobalt (Co); and
the medium-protecting layer is composed of a coating that includes carbon as a main component and nitrogen contained in a surface layer at a number ratio (N/C) of nitrogen (N) atoms and carbon (C) atoms of 0.050 to 0.150, and in a spectrum removed fluorescence from a Raman spectrum in wavenumbers of 900 to 1800 cm −1 obtained by exciting the medium-protecting layer with argon ion laser light having a 514.5 nm wavelength, a peak ratio Dh/Gh when a D peak Dh appearing near 1350 cm −1 and a G peak Gh appearing near 1520 cm −1 are waveform-separated by a Gaussian function is 0.70 to 0.95,
said medium further comprising a soft magnetic layer below the magnetic recording layer, wherein the soft magnetic layer is formed so as to have an antiferromagnetic exchange coupling (AFC) structure containing 30 to 70 at % iron (Fe) and has a saturation magnetization Ms of 1.2 T or more.
3. The perpendicular magnetic recording medium according to claim 2 , wherein the soft magnetic layer has an exchange coupling magnetic field Hex of 40 Oe or more.
4. A perpendicular magnetic recording medium comprising:
a substrate;
a magnetic recording layer on the substrate, and
a medium-protecting layer on the magnetic recording layer, wherein
the magnetic recording layer is a ferromagnetic layer of a granular structure having grain boundaries formed by a non-magnetic material among crystalline particles grown in a columnar shape and containing at least cobalt (Co);
the medium-protecting layer is composed of a coating that includes carbon as a main component and nitrogen contained in a surface layer at a number ratio (N/C) of nitrogen (N) atoms and carbon (C) atoms of 0.090 to 0.150, and in a spectrum removed fluorescence from a Raman spectrum in wavenumbers of 900 to 1800 cm −1 obtained by exciting the medium-protecting layer with argon ion laser light having a 514.5 nm wavelength, a peak ratio Dh/Gh when a D peak Dh appearing near 1350 cm −1 and a G peak Gh appearing near 1520 cm −1 are waveform-separated by a Gaussian function is no less than 0.75 to less than 0.95,
said medium further comprising a capped layer on the magnetic recording layer having a composition different from that of the magnetic recording layer and a perpendicular magnetic anisotropy, and
the magnetic recording layer is formed so as to have a granular structure.
5. The perpendicular magnetic recording medium according to claim 4 , wherein the capped layer has a composition of CoCrPtB.
6. The perpendicular magnetic recording medium according to claim 1 , wherein the medium-protecting layer has increased diamond-like bonds resulting from heating the magnetic layer immediately before forming the medium protecting layer within a temperature range of 157° C.-204° C., with regard to a medium protecting layer that is not heated above 120° C. before forming the medium protecting layer.
7. The perpendicular magnetic recording medium according to claim 4 , wherein the medium-protecting layer has increased diamond-like bonds resulting from heating the magnetic layer immediately before forming the medium protecting layer within a temperature range of 157° C.-204° C., with regard to a medium protecting layer that is not heated above 120° C. before forming the medium protecting layer.