Method of producing a conductive polymer film
View Patent ↗A conductive polymer film is produced by drying out a solution of conductive polymer and a dopant thereof to obtain a dried film. A dried film obtained from the solution is treated, in a reaction vessel, with an organic solvent and pressurized carbon dioxide.
1. A method of producing a conductive polymer film comprising the steps of:
drying a solution of a conductive polymer and a dopant thereof to obtain a dried film;
and treating, in a reaction vessel, the dried film obtained from the solution with a predetermined organic solvent and pressurized carbon dioxide.
2. A method of producing a conductive polymer film according to claim 1 , wherein the pressurized carbon dioxide is subcritical or supercritical carbon dioxide, liquefied carbon dioxide, or pressurized carbon dioxide gas.
3. A method of producing a conductive polymer film according to claim 2 , wherein the pressurized carbon dioxide is subcritical or supercritical carbon dioxide, and the dried film is treated in a uniform phase made by the organic solvent and subcritical or supercritical carbon dioxide.
4. A method of producing a conductive polymer film according to claim 2 , wherein the pressurized carbon dioxide is a liquefied carbon dioxide, and the dried film is treated in a liquid phase made by the liquefied carbon dioxide and the organic solvent.
5. A method of producing a conductive polymer film according to claim 2 , wherein the pressurized carbon dioxide is the pressurized carbon dioxide gas, and the dried film is treated in a vapor phase made by the pressurized carbon dioxide gas and the organic solvent.
6. A method of producing a conductive polymer film according to claim 5 , wherein the pressurized carbon dioxide gas has a pressure of 0.1 MPa to 7.0 MPa.
7. A method of producing a conductive polymer film according to claim 1 , wherein the conductive polymer is poly-3,4-ethylenedioxythiophene and the dopant is polystyrene sulfonic acid.
8. A method of producing a conductive polymer film according to claim 1 , wherein the organic solvent comprises a highly polar solvent.
9. A method of producing a conductive polymer film according to claim 8 , wherein the organic solvent comprises methanol, ethylene glycol, or dimethyl sulfoxide.
10. A method of producing a conductive polymer film according to claim 1 , further comprising the step of removing the organic solvent remaining on the dried film after the treatment step.