Water dispersible polymer compositions
View Patent ↗The water dispersibility of water-soluble polymer particles can be improved by a method which comprises the following step: i) foaming a fluid composition comprising a compound A) having a weight average molecular weight of less than 10,000 or a water-insoluble polymer B) having a weight average molecular weight of at least 10,000; ii) contacting the produced foam with water-soluble polymer particles having a weight average molecular weight of at least 10,000; and iii) drying the particles, whereby the foam collapses during the contacting and/or drying step and the water-soluble polymer particles are encrusted with the compound having a weight average molecular weight of less than 10,000 or the water-insoluble polymer having a weight average molecular weight of at least 10,000.
1. A process for producing a water dispersible polymer composition comprising the steps of
i) foaming a fluid composition comprising a foaming agent and a water insoluble compound A) having a weight average molecular weight of less than 10,000 or a water-insoluble polymer having a weight average molecular weight of at least 10,000, wherein the fluid composition does not include sugars;
ii) contacting the produced foam with water-soluble polymer particles having a weight average molecular weight of at least 10,000 selected from water-soluble carboxy-C 1 -C 3 -alkyl cellulose, carboxy-C 1 -C 3 -alkyl hydroxy-C 1 -C 3 -alkyl cellulose, C 1 -C 3 -alkyl cellulose, C 1 -C 3 -alkyl hydroxy-C 1-3 -alkyl cellulose, hydroxy-C 1-3 -alkyl cellulose, mixed hydroxy-C 1 -C 3 -alkyl cellulose, or mixed C 1 -C 3 -alkyl cellulose; and
iii) drying the particles, whereby the foam collapses during the contacting and/or drying step and the water-soluble polymer particles are encrusted with the compound A) or the water-insoluble polymer B).
2. The process of claim 1 wherein the water-soluble polymer particles are encrusted with calcium carbonate or titanium dioxide.
3. The process of claim 1 wherein the water-insoluble polymer B) is an ethyl cellulose or a water-insoluble homo- or copolymer of styrene, ethylene, propylene, (meth)acrylate or ethylene terephthalate.
4. The process of claim 1 , wherein compound A) is gypsum, mineral oxides, clays, metal oxides, quartz, silica, titanium dioxide, fly ash, hollow fly ash, hollow ceramic spheres, vermiculite, perlite, calcium silicate hydrate or calcium carbonate.