Anode current collector, anode, and secondary battery
View Patent ↗A secondary battery that has superior safety and is able to provide more favorable cycle characteristics is provided. A laminated body in which a cathode and an anode are layered with a separator impregnated with an electrolytic solution in between is contained in a package can and a package cup. In the anode, an anode active material layer containing an anode active material such as silicon is provided on an anode current collector in which projection sections are formed on a base material. The base material contains carbon and sulfur respectively having a content ratio of 100 ppm or less, and contains crystallites having an average diameter of from 0.01 μm to 5 μm both inclusive.
1. An anode comprising:
an anode current collector including an electrolytic copper foil which contains carbon and sulfur respectively having a content ratio of 100 ppm or less, and in which an average diameter of crystallites is from 0.01 μm to 5 μm both inclusive; and
an anode active material layer provided on the anode current collector.
2. The anode according to claim 1 , wherein the anode active material layer contains one or more selected from the group consisting of a simple substance and a compound of silicon as an anode active material.
3. The anode according to claim 1 , wherein the anode active material layer is formed by vapor-phase deposition method.
4. A secondary battery comprising:
a cathode;
an anode; and
an electrolyte,
wherein the anode has an anode current collector and an anode active material layer provided on the anode current collector, and
the anode current collector included an electrolytic copper foil which contains carbon and sulfur respectively having a content ratio of 100 ppm or less, and in which an average diameter of crystallites is from 0.01 μm to 5 μm both inclusive.
5. The secondary battery according to claim 4 , wherein the electrolyte contains one or more of 4-fluoro-1,3-dioxolane-2-one and 4,5-difluoro-1,3-dioxolane-2-one as a solvent.
6. The secondary battery according to claim 4 , wherein the electrolyte contains an electrolyte salt containing one or both of lithium hexafluorophosphate (LiPF 6 ) and lithium tetrafluoroborate (LiBF 4 ).
7. The secondary battery according to claim 4 , wherein the electrolyte contains one or both of sulfobenzoic anhydride and sulfopropionic anhydride.