Helmets comprising ceramic for protection against high energy fragments and rifle bullets
View Patent ↗Helmets for military and other applications that require resistance to high energy fragments and rifle bullets are disclosed. The helmets are fabricated with a combination of ceramic, either as a monolith or as a plurality of discreet pieces, and an inner backing material having a plurality of fibrous layers such as polyolefin and/or aramid fiber layers.
1. A helmet that is resistant to high energy fragments and bullets, the helmet including a rounded shell, said shell comprising a crown and a peripheral surface which define an interior volume, and said rounded shell comprising from the outside to the inside:
(a) an outer layer comprising a ceramic, wherein the ceramic is in the form of a continuous monolith that conforms to a curved shape of the rounded shell; and
(b) an inner backing material comprising a plurality of fibrous layers;
wherein the fibrous layers comprise high tenacity fibers in a resin matrix, and
wherein the inner backing material comprises a fabric having both warp and fill directions, said fabric having about 5.9 to about 21.6 fiber ends per cm in both said warp and fill directions.
2. The helmet of claim 1 , wherein the outer layer consists of an unreinforced, all ceramic component, where said ceramic consists of a compound selected from the group consisting of unreinforced aluminum oxide, boron carbide, silicon carbide, silicon nitride, and titanium diboride.
3. The helmet of claim 1 , wherein the outer layer comprises a reinforced ceramic composited with a non-ceramic fibrous material, wherein said outer layer comprises at least about 70% ceramic by weight.
4. The helmet of claim 1 , wherein the high tenacity fibers comprise polyethylene fibers having a tenacity equal to or greater than about 35 g/d.
5. The helmet of claim 1 , wherein the shell further comprises a shock absorbing material layer, disposed outside the outer layer, and comprising a closed cell foam.
6. The helmet of claim 1 , wherein the ceramic and the inner backing material are present in amounts, respectively, from about 30% to about 85% by weight of the shell and from about 10% to about 50% by weight of the shell.
7. The helmet of claim 1 , wherein the outer layer and inner backing material each have the shape of a rounded helmet shell defining an interior volume, wherein said continuous monolith consists essentially of a ceramic, single, continuous solid piece that completely covers the inner backing material, wherein said ceramic monolith has a thickness of from about 4 mm (0.16 in) to about 6 mm (0.24 in).
8. The helmet of claim 1 , wherein the shell has an areal density from about 14.7 kg/m 2 (3 lb/ft 2 ) to about 24.5 kg/m 2 (5 lb/ft 2 ).
9. The helmet of claim 1 , wherein the outer layer comprises a reinforced ceramic composited with a non-ceramic, non-fibrous material, wherein said outer layer comprises at least about 70% ceramic by weight.
10. A method for forming a rounded shell for a helmet that is resistant to high energy fragments and bullets, said rounded shell comprising a crown and a peripheral surface which define an interior volume, the method comprising:
(a) supplying, to a mold, an outer layer comprising a ceramic, an inner backing material comprising a plurality of fibrous layers, and an adhesive layer to a mold, wherein the adhesive layer is disposed between the outer layer and the inner backing material, wherein the ceramic is in the form of a continuous monolith that conforms to a curved shape of the rounded shell, or wherein the ceramic is in the form of a plurality of ceramic plates that conform to a curved shape of the rounded shell, wherein some or all of the ceramic plates have a non-planar shape; and
(b) applying heat and pressure to the outer layer, inner backing material, and adhesive to bond the ceramic to the inner backing material and form the rounded shell.
11. A molded, rounded helmet shell prepared according to the method of claim 10 , wherein said ceramic covers only a portion of said inner backing material such that only the crown of the shell or only the peripheral surface of the shell is covered by said ceramic.
12. A helmet that is resistant to high energy fragments and bullets, the helmet including a rounded shell, said shell comprising a crown and a peripheral surface which define an interior volume, and said rounded shell comprising from the outside to the inside:
(a) an outer layer comprising a ceramic, wherein the ceramic is in the form of a plurality of ceramic plates that conform to a curved shape of the rounded shell, wherein some or all of the ceramic plates have a non-planar shape; and
(b) an inner backing material comprising a plurality of fibrous layers, wherein the fibrous layers comprise high tenacity fibers, wherein said high tenacity fibers are optionally in a resin matrix, and wherein said high tenacity fibers comprise polyethylene fibers having a tenacity equal to or greater than about 35 g/d.
13. The helmet of claim 12 , wherein adjacent ceramic plates are mechanically fitted or chemically bonded with one another at their adjacent borders, whereby the adjacent plates physically abut each other at their adjacent borders, and wherein said mechanically fitted or chemically bonded ceramic plates cover only a portion of said inner backing material.
14. The helmet of claim 12 wherein all of the ceramic plates have a non-planar shape, and wherein said ceramic plates have a substantially uniform thickness, and wherein said ceramic plates have a thickness of from about 4 mm (0.16 in) to about 6 mm (0.24 in).
15. The helmet of claim 13 , wherein the outer layer and inner backing material each have the shape of a rounded helmet shell defining an interior volume, wherein the outer layer covers the inner backing material, and wherein all adjacent ceramic plates are joined with overlapping joints, thereby providing complete ceramic coverage of the inner backing material, and wherein said helmet shell has a thickness of less than about 12 mm.
16. The helmet of claim 1 , wherein the outer layer and inner backing material each have the shape of a rounded helmet shell defining an interior volume, wherein said continuous monolith consists of an all ceramic, single, continuous solid piece that covers the inner backing material, thereby providing complete ceramic coverage of the inner backing material, and wherein said helmet shell has a thickness of less than about 14 mm.
17. A molded, rounded helmet shell prepared according to the method of claim 10 , wherein the outer layer comprises a reinforced ceramic composited with a non-ceramic fibrous material, wherein said outer layer comprises at least about 70% ceramic by weight.
18. A molded, rounded helmet shell prepared according to the method of claim 10 , wherein the fibrous layers comprise high tenacity fibers, wherein said high tenacity fibers are optionally in a resin matrix, and wherein said high tenacity fibers comprise polyethylene fibers having a tenacity equal to or greater than about 35 g/d.
19. The helmet of claim 12 wherein the fibrous layers comprise high tenacity fibers in a resin matrix, and wherein the inner backing material comprises a fabric having both warp and fill directions, said fabric having about 5.9 to about 21.6 fiber ends per cm in both said warp and fill directions.
20. The helmet of claim 12 wherein the outer layer comprises a reinforced ceramic composited with a non-ceramic fibrous material, wherein said outer layer comprises at least about 70% ceramic by weight.