View Patent ↗The present invention provides sintered composite polymeric materials and methods of making and using the same. The sintered composite polymeric materials are made by sintering composite particles comprising a polytetrafluoroethylene component and a carbonaceous component, wherein the carbonaceous component is dispersed throughout the polytetrafluoroethylene component.
1. A method of making a sintered porous membrane comprising a two-step method comprising:
a first step comprising providing a PTFE component comprising a plurality of PTFE particles;
providing a carbonaceous component;
mixing the PTFE component and the carbonaceous component to form a mixture;
heating the mixture to a temperature of about the microcrystalline melting point of the PTFE component to form a thermally treated material wherein the individual PTFE particles of the PTFE component are softened and are not completely fused together and wherein the carbonaceous component is dispersed throughout the PTFE component; and
a second step comprising breaking the thermally treated material into composite particles comprising a PTFE component and a carbonaceous component dispersed throughout the PTFE component;
providing a plurality of the composite particles;
disposing the plurality of the composite particles in a mold;
applying a compressive force to the composite particles;
relieving the compressive force on the composite particles;
heating the composite particles to a temperature above the microcrystalline melting point of the PTFE component to form a porous composite material;
cooling the porous composite material;
removing the porous composite material from the mold, and
skiving the porous composite material to make a membrane.
2. The method of claim 1 , wherein the temperature is from about 320° C. to about 380° C.
3. The method of claim 1 , wherein the compressive force is from about 40 kgm/cm 2 to about 900 kgm/cm 2 .
4. The method of claim 1 , wherein the carbonaceous component comprises black polymeric materials, black inks, black coatings, or particulate carbonaceous materials selected from the group consisting of carbon black, graphite, amorphous carbon, carbon fiber, active carbon, and carbon nanotubes, or mixtures thereof.
5. The method of claim 4 , wherein the particulate carbonaceous material is carbon black.
6. A sintered porous membrane made by the method of claim 1 .
7. The membrane of claim 6 , comprising a porosity ranging from about 10 percent to about 90 percent.
8. The membrane of claim 6 , comprising a first surface and a second surface, wherein the first surface has a lighter color than the second surface.
9. The membrane of claim 8 , wherein the first surface has a spectral reflectance of greater than about 90 percent and the second surface has a spectral reflectance of less than about 20 percent.
10. The membrane of claim 6 , comprising an average pore size ranging from about 0.1 μm to about 500 μm, and a porosity ranging from about 10 percent to about 90 percent.
11. The membrane of claim 10 , comprising an electrical resistance of greater than about 10 16 ohm/m.
12. The membrane of claim 10 , comprising an electrical resistance of less than about 10 12 ohm/m.
13. The membrane of claim 10 , wherein the membrane comprises an average pore size from about 0.1 μm to about 100 μm.
14. The membrane of claim 6 , wherein the membrane is a black colored membrane.
15. The membrane of claim 6 , wherein the membrane is an electrostatic conductive membrane.
16. The membrane of claim 6 , wherein the membrane comprises a thickness of about 50 μm to about 5 mm.
17. The membrane of claim 6 , wherein the membrane comprises a pore size from about 0.5 μm to about 50 μm.
18. The membrane of claim 6 , wherein the membrane comprises a porosity from about 20% to about 60%.
19. The method of claim 1 , wherein the mixture of the PTFE component and the carbonaceous component comprises from about 1 weight percent to about 30 weight percent carbonaceous component.