Solar reflective coatings and coating systems

1. A coating composition comprising:

(a) a film-forming resin;

(b) colored and/or opaque infrared reflective pigment particles;

(c) infrared transparent pigment particle; and

(d) a tri-block copolymer pigment dispersant;

wherein the colored and/or opaque infrared reflective pigment and the infrared transparent pigment are separate and different components and are separately dispersed in the coating composition and wherein the coating composition, when formed into a cured coating, exhibits:

(1) a total solar reflectance of at least 15% as measured in accordance with ASTM E 903-96; and

(2) an angle dependent color change of no more than 5 ΔE units at a viewing angle from 110° to −15° when compared to the color of a control coating not containing the colored and/or opaque infrared reflective pigment particles (b).

2. The coating composition of claim 1 , wherein the cured coating further exhibits an angle dependent CIELAB L* value of no more than 50 at an observation angle of 25°.

3. The coating composition of claim 2 , wherein the angle dependent CIELAB L* value is no more than 25.

4. The coating composition of claim 1 , wherein the total solar reflectance is at least 25%.

5. The coating composition of claim 1 , wherein the tri-block copolymer comprises:

(a) a first segment comprising infrared transparent pigment affinic groups;

(b) a second segment comprising polar groups; and

(c) a third segment which is different from the first segment and the second segment.

6. The coating composition of claim 5 , wherein the infrared transparent pigment affinic groups comprise aromatic groups.

7. The coating composition of claim 5 , wherein the third segment is substantially non-polar and substantially free of infrared transparent pigment affinic groups.

8. The coating composition of claim 1 , wherein the tri-block copolymer pigment dispersant has a polymer chain structure represented by the general formula:

φ-(G) p -(W) q -(Y) s -T

wherein:

(a) G is a residue of at least one radically polymerizable ethylenically unsaturated monomer;

(b) W and Y are residues of at least one radically polymerizable ethylenically unsaturated monomer; with W and Y being different from one another;

(c) φ is a hydrophobic residue of or derived from an initiator and is free of a radically transferable group of the initiator;

(d) T is or is derived from the radically transferable group of the initiator; and

(e) p, q, and s are each individually selected such that the pigment dispersant has a number average molecular weight of at least 250.

9. The coating composition of claim 1 , wherein the tri-block copolymer pigment dispersant comprising:

(i) a first block comprising an oxirane functional monomer reacted with a carboxylic acid;

(ii) a second block comprising (meth)acrylic acid alkyl esters; and

(iii) a third block comprising (meth)acrylic acid alkyl esters.

10. The coating composition of claim 1 , wherein the infrared reflective pigment particles have a ratio of reflectivity in the near-infrared region to reflectivity in the visible region of greater than 1:1.

11. The coating composition of claim 1 , wherein the infrared reflective pigment particles comprise an interference pigment.

12. The coating composition of claim 1 , wherein the infrared transparent pigment particles comprise an organic pigment.

13. The coating composition of claim 12 , wherein the organic pigment comprises aromatic groups.

14. The coating composition of claim 13 , wherein the organic pigment comprises a perylene-based pigment.

15. A multi-component composite coating comprising:

(a) a first coating exhibiting a CIELAB L* value of no more than 50 and a total solar reflectance of at least 15% as measured in accordance with ASTM E 903-96 and deposited from a first coating composition comprising:

(i) a film-forming resin;

(ii) colored and/or opaque infrared reflective pigment particles;

(iii) infrared transparent pigment particles; and

(iv) a tri-block copolymer pigment dispersant;

wherein the colored and/or opaque infrared reflective pigment and the infrared transparent pigment are separate and different components and are separately dispersed in the first coating composition, and

wherein the first coating composition, when formed into a cured coating, exhibits an angle dependent color change of no more than 5 ΔE units at a viewing angle from 110° to −15° when compared to the color of a control coating not containing the infrared reflective pigment particles (ii); and

(b) a second coating deposited beneath at least a portion of the first coating, the second coating being deposited from a second coating composition comprising:

(i) a film-forming resin;

(ii) infrared reflective flake pigment particles; and

(iii) infrared reflective inorganic oxide pigment particles;

wherein the infrared reflective flake pigment and the infrared reflective inorganic oxide pigment are separate and different components of the second coating coating composition.

16. The composite coating of claim 15 , wherein the sum of (b)(ii) and (b)(iii) in the second coating composition from which the second coating is deposited is no more than 10% by weight, based on the total solids weight of the second coating composition.