Storage-stable, hydroxy-modified microgel latices
View Patent ↗A composition is described, encompassing a constituent selected from the group consisting of a modified resin acid (I), a fatty acid (II) and a mixture composed of a modified resin acid (I) and of a fatty acid (II), where the degree of neutralization of the constituent is from 104 to 165%. Its use for the production of microgels is also described.
1. A process for the production of a microgel, comprising:
polymerizing, via emulsion polymerization, monomers in the presence of an emulsifier, wherein said emulsifier comprises a mixture of a modified resin acid and a fatty acid, wherein the degree of neutralisation of the mixture is from 106 to 145%, thereby forming said microgel.
2. The process according to claim 1 , wherein the monomers are selected from the group consisting of conjugated dienes, vinylaromatic monomers, crosslinking monomers, and monomers containing hydroxy groups.
3. The process according to claim 1 , further comprising after said polymerization, coagulation of the microgel at temperatures above the glass transition temperature of the microgel.
4. The process according to claim 3 , wherein the coagulation is carried out at a temperature which is higher by at least 10° C. than the glass transition temperature of the microgel.
5. The microgel obtained by the process according to claim 1 .
6. The microgel according to claim 5 , wherein said microgel has more than 70% by weight gel content.
7. The microgel according to claim 5 , wherein the microgel has a swelling index of less than 30.
8. The microgel according to claim 5 , wherein the microgel has more than 0.1% by weight content of copolymerised monomers containing hydroxy groups.
9. The microgel according to claim 8 , wherein the microgel has a hydroxy number greater than 0.5.