Light-weight proppant from heat-treated pumice
View Patent ↗A process for forming a strong, low-density proppant, which process includes heating pumice particulates, or shaped agglomerates thereof, so as to form heat-treated pumice particulates, or heat-treated, shaped pumice agglomerates, having an apparent density of 2.4 or less and a crush resistance of no more than 10% fines at 4000 psi. Proppants, and well treatment fluids comprising proppants, meeting these characteristics and processes for treating subterranean formations using fluids which include such proppants are also described.
1. A process for forming a proppant, the process comprising
heating an amount of pumice particulates coated with bentonite clay so as to (i) increase its density and maintain or shrink its size relative to the pre-heated pumice particulates and (ii) form an amount of heat-treated, pumice particulates having an apparent density of 2.4 or less, and a crush resistance of no more than 10% fines at 4000 psi;
wherein the amount of bentonite clay is in the range of about 50 to 200 wt %, based on the weight of the shaped pumice agglomerates in dry form.
2. The process according to claim 1 , wherein the pumice particulates have an average particle size of greater than 150 microns.
3. The process according to claim 1 , wherein the heating step is conducted at a treatment temperature of at least 1050° C.
4. The process according to claim 1 , further comprising coating the heat-treated particulates with a secondary organic coating.
5. A process according to claim 1 , further comprising
agglomerating and shaping the amount of pumice particulates prior to heating, so as to form an amount of shaped pumice agglomerates;
wherein the step of heating is carried out with respect to the shaped pumice agglomerates, so as to form an amount of heat-treated, shaped pumice agglomerates having an apparent density of 2.4 or less, and a crush resistance of no more than 10% fines at 4000 psi.
6. The process according to claim 5 , wherein the agglomerating and shaping step is carried out by a process comprising contacting the pumice particles with a binder.
7. The process according to claim 6 , wherein the binder is an organic binder.
8. The process according to claim 7 , wherein the organic binder is comprised of one or more components selected from the group consisting of starch, polyvinyl alcohol, gum arabic, lignosulfonates, molasses, dextrins, poly vinyl pyrrolidone, acrylics, polyethyleneimine, a methyl cellulose, a hydroxypropylmethyl cellulose, a hydroxyethyl cellulose, sodium alginate, polyacrylamide, xanthan gum, and guar gum.
9. The process according to claim 8 , wherein the organic binder comprises sodium carboxymethyl cellulose.
10. The process according to claim 7 , wherein the amount of binder is no more than about 10 wt %, based on the weight of the pumice particulates in dry form.
11. The process according to claim 5 , wherein pumice particulates have an average particle size of no more than 150 microns.
12. The process according to any one of claims 5 to 11 , further comprising coating the heat-treated, shaped pumice agglomerates with either an inorganic coating or an organic coating, or both.
13. The process according to any one of claims 2 to 11 , wherein the pumice particulates have a mean particle size distribution (D 50 ) of less than 200 microns.
14. A process for forming a proppant, the process comprising agglomerating and shaping an amount of pumice particulates so as to form an amount of shaped pumice agglomerates; coating the shaped pumice agglomerates with bentonite clay, wherein the amount of bentonite clay is in the range of about 50 to 200 wt %, based on the weight of the shaped pumice agglomerates in dry form, to form coated agglomerates, and then heating the coated agglomerates so as to (i) increase the density and to maintain or shrink the size of the pumice particulates relative to pre-heating and (ii) to form an amount of heat-treated, shaped pumice agglomerates having an apparent density of 2.4 or less, and a crush resistance of no more than 10% fines at 4000 psi.
15. The process according to claim 14 , wherein the heating step is conducted at a treatment temperature of at least 1050° C.
16. The process according to claim 14 , further comprising coating the heat-treated, coated agglomerates with a secondary organic coating.
17. The process according to claim 14 , wherein the pumice particulates have a mean particle size distribution (D 50 ) of less than 200 microns.
18. A proppant formed by a process in accordance with claim 1 .
19. A process comprising treating a subterranean formation with a well treatment fluid comprising a proppant formed by a process in accordance with claim 1 .
20. The process according to claim 19 , wherein the pumice particulates have an average particle size of greater than 150 microns.
21. The process according to claim 19 , wherein the heating step is conducted at a treatment temperature of at least 1050° C.
22. The process according to claim 19 , further comprising coating the heat-treated particulates with a secondary organic coating.
23. The process according to claim 19 , further comprising
agglomerating and shaping the amount of pumice particulates prior to heating, so as to form an amount of shaped pumice agglomerates;
wherein the step of heating is carried out with respect to the shaped pumice agglomerates, so as to form an amount of heat-treated, shaped pumice agglomerates having an apparent density of 2.4 or less, and a crush resistance of no more than 10% fines at 4000 psi.
24. The process according to claim 23 , wherein the agglomerating and shaping step is carried out by a process comprising contacting the pumice particles with a binder.
25. The process according to claim 24 , wherein the binder is an organic binder.
26. The process according to claim 25 , wherein the organic binder is comprised of one or more components selected from the group consisting of starch, polyvinyl alcohol, gum arabic, lignosulfonates, molasses, dextrins, poly vinyl pyrrolidone, acrylics, polyethyleneimine, a methyl cellulose, a hydroxypropylmethyl cellulose, a hydroxyethyl cellulose, sodium alginate, polyacrylamide, xanthan gum, and guar gum.
27. The process according to claim 26 , wherein the organic binder comprises sodium carboxymethyl cellulose.
28. The process according to claim 25 , wherein the amount of binder is no more than about 10 wt %, based on the weight of the pumice particulates in dry form.
29. The process according to claim 23 , wherein pumice particulates have an average particle size of no more than 150 microns.
30. The process according to claim 29 , further comprising coating the heat-treated, shaped pumice agglomerates with either an inorganic coating or an organic coating, or both.
31. The process according to claim 23 , further comprising coating the heat-treated, shaped pumice agglomerates with either an inorganic coating or an organic coating, or both.
32. The process according to claim 20 , wherein the pumice particulates have a mean particle size distribution (D 50 ) of less than 200 microns.
33. The process according to claim 29 , wherein the pumice particulates have a mean particle size distribution (D 50 ) of less than 200 microns.