Sugar production by decrystallization and hydrolysis of polysaccharide enriched biomass
View Patent ↗Sugar solutions are obtained from polysaccharide enriched biomass by contacting biomass with water and at least one nucleophilic base to produce a polysaccharide enriched biomass comprising a solid fraction and a liquid fraction. The solid fraction is separated from the lignin-containing liquid fraction and contacted with an acid solution, the acid solution comprising about 70 weight percent to about 100 weight percent sulfuric acid or an acid mixture comprising phosphoric acid and sulfuric acid, at a temperature and for a reaction time sufficient to produce a decrystallized biomass mixture. Water is added and the diluted biomass mixture is then hydrolyzed to produce a saccharification product comprising sugars.
1. A process to produce a sugar solution from polysaccharide enriched biomass, the process comprising:
a) providing a biomass comprising lignin and having a glucan/xylan weight ratio G 1 /X 1 ;
b) contacting the biomass of (a) with water and at least one nucleophilic base, to form a biomass slurry having a pH of about 12.5 to about 13.0; and
c) maintaining the biomass slurry under reaction conditions comprising a first temperature and first reaction time such that the slurry attains a pH of about 9.5 to about 10.0, wherein the slurry comprises a lignin-containing liquid fraction and a solid fraction comprising a polysaccharide enriched biomass wherein the biomass slurry has a glucan/xylan weight ratio G 2 /X 2 within about 15% of the value of G 1 /X 1 ;
wherein G 1 and G 2 are grams of glucan per 100 grams of biomass and of biomass slurry respectively, and X 1 and X 2 are grams of xylan per 100 grams of biomass and biomass slurry respectively;
d) contacting the polysaccharide enriched biomass solid fraction with an acid solution at a second temperature and for a second reaction time sufficient to produce a decrystallized biomass mixture, wherein the polysaccharides present in the polysaccharide enriched biomass solid fraction have been substantially decrystallized, and wherein the acid solution;
i) comprises about 70 weight percent to about 100 weight percent sulfuric acid; or
ii) comprises an acid mixture comprising phosphoric acid and sulfuric acid, wherein the molar ratio of phosphoric acid to sulfuric acid in the acid mixture is from about 3.39:1 to about 0.21:1;
e) adding water to the decrystallized biomass mixture to produce a diluted biomass mixture, wherein the amount of water added is from about 20 weight percent to about 200 weight percent based on the weight of the decrystallized biomass mixture; and
f) maintaining the diluted biomass mixture at a third temperature and for a third reaction time to produce a saccharification product comprising a sugar solution.
2. The process of claim 1 , wherein the at least one nucleophilic base comprises a water soluble metal hydroxide, optionally in combination with a metal carbonate or an organic hydroxide.
3. The process of claim 2 wherein the water soluble metal hydroxide is selected from the group consisting of sodium hydroxide or potassium hydroxide and the metal carbonate or an organic hydroxide is selected from the group consisting of sodium carbonate, potassium carbonate ammonium hydroxides and alkyl substituted ammonium hydroxide.
4. The process of claim 1 , wherein the first temperature is from about 20° C. to about 110° C.
5. The process of claim 1 , wherein the first reaction time is from about 4 hours to about 30 days.
6. The process of claim 1 , wherein the value of G 2 /X 2 is within 10% of the value of G 1 /X 1 .
7. The process of claim 1 , wherein at least about 70 percent of the lignin in the provided biomass is delignified in the polysaccharide enriched biomass solid fraction.
8. A process according to claim 1 wherein step (e) is performed one or more times.
9. The process of claim 1 , wherein the second temperature is from about 0° C. to about 30° C. and the second reaction time is from about 0.1 hours to about 48 hours.
10. The process of claim 1 , wherein the third temperature is from about 50° C. to about 100° C. and the third reaction time is from about 1 hour to about 8 hours.
11. The process of claim 1 , wherein the acid solution comprises about 70 weight percent to about 100 weight percent sulfuric acid.
12. The process of claim 1 , wherein the acid solution comprises the acid mixture comprising phosphoric and sulfuric acid, and the molar ratio of phosphoric acid to sulfuric acid in the acid mixture is from about 1.98:1 to about 0.36:1.
13. The process of claim 1 , wherein the ratio of the weight of the polysaccharide enriched biomass solid fraction to the weight of the acid solution is from about 1:0.2 to about 1:5.
14. The process of claim 1 , further comprising separating at least a portion of the sugars from the saccharification product.