Hyper-branched polyester for use in CPT toner and method of preparing the same
View Patent ↗A hyper-branched polyester and a method of making the same having a tri-functional monomer A3, a di-functional monomer B2 and a mono-functional monomer C1 having a monomer ratio of A3:B2:C1 from about 1:0.2:2 to about 1:1.4:0.2 for use in a chemically processed electrophotographic toner providing a lower fusing temperature. In one form, the hyper-branched polyester includes a tri-hydroxy monomer, a di-acid and its derivatives, and a mono-acid and its derivatives. In other forms, a substituted anhydride and a long chain hydrocarbon carboxylic acid and its derivatives may also be included in the di-functional monomer.
1. A hyper-branched polyester consisting of
a tri-hydroxyl monomer A3, selected from a group consisting of glycerol and trimethanolpropane, a di-acid monomer B2, selected from the group consisting of a dodecenyl succinic anhydride and a 2-dodecen-1-yl-succinic anhydride, and a mono-acid monomer C1, wherein a molar ratio of A3:B2:C1 is from about 1:0.2:2 to about 1:1.4:0.2; and the mono-acid monomer C1 contains a crystallinity functional group having a polyethylene substituted carboxylic acid with carbon chain lengths of C≧25 and the hyper-branched polyester is used in a chemically processed electrophotographic toner.
2. The hyper-branched polyester of claim 1 wherein the monomer ratio of A3:B2:C1 is 1:1:1.
3. The hyper-branched polyester of claim 1 wherein the monomer ratio A3:B2:C1 is 1:0.75:1.
4. A method of making a hyper-branched polyester of claim 1 comprising:
making a mixture of a tri-hydroxyl monomer A3, a di-acid monomer B2 and a mono-acid monomer C1, wherein a molar ratio of A3:B2:C1 is from about 1:0.2:2 to about 1:1.4:0.2
and heating the mixture to a first temperature of about 100° C. until all the components are melted and mixed
under nitrogen gas, increasing the temperature of the mixture to a second temperature of about 150° C. and holding the mixture at the second temperature for about two hours;
increasing the temperature of the mixture to a third temperature of about 220° C. and holding the mixture at the third temperature for about four hours; and
returning the mixture to room temperature.
5. The method of claim 4 wherein the monomer ratio of A3:B2:C1 is 1:1:1.
6. The method of claim 4 wherein the monomer ratio A3:B2:C1 is 1:0.75:1.
7. The method of claim 4 further comprising providing dibutyltin dilaurate as a catalyst during raising the temperature of the mixture to the first temperature.