Thermoplastic elastomer composition
A thermoplastic elastomer composition comprises (A) about 25 to about 55 parts by weight of a block terpolymer including an aromatic vinyl compound and an alkene compound; (B) about 20 to about 50 parts by weight of a paraffin oil; (C) about 5 to about 15 parts by weight of a polyolefin resin; (D) about 5 to about 20 parts by weight of an inorganic additive; and (E) about 3 to about 15 parts by weight of a polyphenylene ether. The thermoplastic elastomer composition can have excellent physical properties, such as flexibility (or resilience), surface hardness, and restoring force at high temperatures.
1. A thermoplastic elastomer composition comprising:
(A) about 25 to about 55 parts by weight of block terpolymer including an aromatic vinyl compound and an alkene compound, wherein said block terpolymer (A) is a A-B-A′ block terpolymer, wherein each of the A and A′ blocks are a hard segment, the B block is a soft segment, and the terpolymer comprises the hard segments in an amount of about 20 to about 35% by weight and the soft segment in an amount of about 65 to about 80% by weight;
(B) about 20 to about 50 parts by weight of a paraffin oil;
(C) about 5 to about 15 parts by weight of a polyolefin resin;
(D) about 5 to about 20 parts by weight of a inorganic additive; and
(E) about 3 to about 15 parts by weight of a polyphenylene ether,
wherein said thermoplastic elastomer composition has a surface hardness of about 50A (shore A) or less and has an elongation permanent set (100° C.) of about 5 to about 13%.
2. The thermoplastic elastomer composition of claim 1 , wherein each of said A and A′ blocks comprises an aromatic vinyl polymer and said B block comprises a conjugated diene polymer.
3. The thermoplastic elastomer composition of claim 1 , wherein said block terpolymer (A) comprises styrene-ethylene butadiene-styrene (SEBS) block terpolymer, styrene-ethylene propylene-styrene (SEPS) block terpolymer, styrene-isoprene-styrene (SIS) block terpolymer, styrene-ethylene isoprene-styrene block terpolymer, styrene-ethylene ethylene propylene-styrene (SEEPS) block terpolymer, or a combination thereof.
4. The thermoplastic elastomer composition of claim 1 , wherein said block terpolymer (A) has a weight average molecular weight of about 140,000 to about 180,000.
5. The thermoplastic elastomer composition of claim 1 , wherein said paraffin oil (B) has a kinematic viscosity of about 95 to about 215 cst (40° C. as a reference).
6. The thermoplastic elastomer composition of claim 1 , wherein said polyolefin resin (C) has a melt index (230° C., 2.16 kg) of about 11 to about 25 g/10 min.
7. The thermoplastic elastomer composition of claim 1 , wherein said polyolefin resin (C) comprises polyethylene, polypropylene, polybutylene, ethylene-propylene copolymer, or a combination thereof.
8. The thermoplastic elastomer composition of claim 1 , wherein said inorganic additive (D) has an average particle size of about 0.01 to about 5 μm.
9. The thermoplastic elastomer composition of claim 1 , wherein said inorganic additive (D) comprises calcium carbonate, talc, clay, silica, mica, titanium dioxide, carbon black, graphite, wollastonite, nano silver, or a combination thereof.
10. The thermoplastic elastomer composition of claim 1 , wherein said polyphenylene ether resin (E) has a weight average molecular weight of about 20,000 to about 40,000.
11. The thermoplastic elastomer composition of claim 1 , further comprising an additive comprising an UV absorbent, heat stabilizer, antioxidant, flame retardant, lubricant, colorant, antimicrobial agent or a combination thereof.
12. A molded article comprising the thermoplastic elastomer composition as defined in claim 1 .
13. A thermoplastic elastomer comprising:
(A) a terpolymer comprising styrene-ethylene butadiene-styrene (SEBS) block terpolymer, styrene-ethylene propylene-styrene (SEPS) block terpolymer, styrene-isoprene-styrene (SIS) block terpolymer, styrene-ethylene isoprene-styrene block terpolymer, styrene-ethylene ethylene propylene-styrene (SEEPS) block terpolymer, or a combination thereof;
(B) a paraffin oil;
(C) a polyolefin resin comprising polyethylene, polypropylene, polybutylene, ethylene-propylene copolymer, or a combination thereof;
(D) an inorganic additive comprising calcium carbonate, talc, or a combination thereof; and
(E) a polyphenylene ether
wherein said thermoplastic elastomer has a surface hardness of about 50A (shore A) or less.
14. The thermoplastic elastomer of claim 13 , wherein said thermoplastic elastomer has a tensile strength (100° C.) of about 14 to about 25 kgf/cm 2 , an elongation rate (100° C.) of about 430 to about 700%, and an elongation permanent set (100° C.) of about 5 to about 13%.
15. A molded article comprising the thermoplastic elastomer of claim 13 .