High resilience flexible polyurethane foam using MDI
View Patent ↗A high resilience flexible polyurethane foam, made using methylene diphenyl diisocyanate (MDI), having a bulk foam density in the range of 2.5 pounds per cubic foot or lower and having a foam hardness or IFD in the range of 10 to 40 lb/50 in 2 . The present invention is also directed to the method for the making thereof.
1. A high resilience flexible polyurethane foam having a bulk foam density of 2.5 pounds per cubic foot or lower and having a foam hardness or 25% Indentation Force Deflection (IFD) in a range of 10 to 40 lb/50 in 2 , wherein the foam results from a reaction of a polyalkyleneoxide polyether glycol polyol having a molecular weight in a range of from about 4,500 to 6,000 g/mol and water with methylene diphenyl diisocyanate (MDI) in the presence of at least a 1,2-dimethylimidazole amine catalyst, a silicone surfactant, and an auxiliary blowing agent and without a tin catalyst and without toluene diisocyanate (TDI), and wherein the foam made without the use of a flame retardant additive passes the requirements of State of California Technical Bulletin 117.
2. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam hardness or 25% IFD is measured in accordance with test method ASTM 3574—Test B 1 .
3. The high resilience flexible polyurethane foam according to claim 1 , wherein the bulk foam density is 1.8 pounds per cubic foot or lower.
4. The high resilience flexible polyurethane foam according to claim 1 , wherein the MDI is pure or comprises a mixture of isomers.
5. The high resilience flexible polyurethane foam according to claim 4 , wherein the mixture is in any amount or in any ratio of isomers selected from the group consisting of 4,4′-diphenylmethane diisocyanate, 2,4′-diphenylmethane diisocyanate, 2,2′-diphenylmethane diisocyanate, and a combination thereof.
6. The high resilience flexible polyurethane foam according to claim 4 , wherein the mixture is blended with a polymeric, modified, or prepolymer MDI species.
7. The high resilience flexible polyurethane foam according to claim 4 , wherein the isomers have a blend average isocyanate functionality of ≧2.
8. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam has an isocyanate index or stoichiometric amount in a range of 70 to 130.
9. The high resilience flexible polyurethane foam according to claim 8 , wherein the foam has an isocyanate index or stoichiometric amount in a range of 90 to 110.
10. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam is made using a high resilience polyether polyol.
11. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam is made without a polyalkyleneoxide polyether polyol of less than about 4000 g/mol molecular weight.
12. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam is made without a graft polyol, copolymer polyol, polymer polyol, PIPA polyol, crosslinker, polyharnstoff dispersion (PHD) polyol, or any combination thereof.
13. The high resilience flexible polyurethane foam according to claim 1 , wherein the polyol is a polyalkyleneoxide polyether glycol polyol having a molecular weight in a range of from about 4,500 to 6,000 g/mol with a weight percent content of ethylene oxide groups content being from about 12 to 20 weight percent of total alkylene oxide group content while having a hydroxyl functionality ranging from about 2 to 8.
14. The high resilience flexible polyurethane foam according to claim 13 , wherein the polyol is a polyalkyleneoxide polyether glycol polyol having a molecular weight in a range of from about 4,500 to 6,000 g/mol with a weight percent content of ethylene oxide groups content being from about 12 to 20 weight percent of total alkylene oxide group content while having a hydroxyl functionality ranging from about 2 to 3.
15. The high resilience flexible polyurethane foam according to claim 1 , wherein the polyol is a polyalkyleneoxide polyether glycol polyol having a molecular weight in a range of from about 4,500 to 6,000 g/mol with 80 to 88 weight percent of total alkylene oxide groups being propylene oxide groups while having a hydroxyl functionality ranging from about 2 to 8.
16. The high resilience flexible polyurethane foam according to claim 1 , wherein the foam is made with or without a load-bearing or support-enhancing polyol selected from the group consisting of copolymer polyol, polymer polyol, graft polyol, PIPA polyol, crosslinker, polyharnstoff dispersion (PHD) polyol, and any combination thereof.
17. The high resilience flexible polyurethane foam according to claim 1 , the foam comprises an additive selected from the group consisting of a flame retardant, a cross-linking agent, a chain-extending agent, melamine, a filler, a pigment, a dye, an antimicrobial, a biocide, an antioxidant, and a combination thereof.
18. A high resilience flexible polyurethane foam having a bulk foam density of 2.5 pounds per cubic foot or lower and having a foam hardness or 25% Indentation Force Deflection (IFD) in a range of 10 to 40 lb/50 in 2 , wherein the foam results from a reaction of a polyalkyleneoxide polyether glycol polyol having a molecular weight in a range of from about 4,500 to 6,000 g/mol and a primary blowing agent of water with methylene diphenyl diisocyanate (MDI) in the presence of at least a 1,2-dimethylimidazole amine catalyst, a silicone surfactant, and an auxiliary blowing agent of acetone, and without a tin catalyst and without toluene diisocyanate (TDI), wherein acetone is in a range of 2 to 10 pphp, and wherein the foam made without the use of a flame retardant additive passes the requirements of State of California Technical Bulletin 117.