Method for superconducting connection between MgB2 superconducting wires via a MgB2 matrix made from a boron powder compressed element infiltrated with Mg
A method for superconductingly connecting two or more wires ( 1, 2 ), each comprising at least one filament ( 3 a - 3 d ) that contains MgB 2 or a mixture of Mg and B, wherein a superconducting connection is realized through exposed end regions ( 4 a ) of the filaments ( 3 a - 3 d ) via an MgB 2 matrix, is characterized in that a bulk boron powder ( 4 ) is provided into which the exposed end regions ( 4 a ) of the filaments ( 3 a - 3 d ) of the wires ( 1, 2 ) project, the boron of the bulk boron powder ( 4 ) being present in amorphous modification. The bulk powder ( 4 ) is then compacted together with the projecting exposed end regions ( 4 a ) of the filaments ( 3 a, 3 b ) to form a compressed element ( 8 ) and the compressed element ( 8 ) is infiltrated with molten magnesium ( 10 ) from the surface ( 13 ) of the compressed element ( 8 ). The method improves the quality, in particular, the current-carrying capacity and the critical magnetic field strength of a superconducting connection of MgB 2 superconducting wires.
1. A method for connecting two or more wires, each wire comprising at least one filament that contains MgB 2 or a mixture of Mg and B, wherein a superconducting connection is realized at exposed end regions of the filaments via an MgB 2 matrix, the method comprising the steps of:
a) inserting the exposed end regions of the filaments into bulk boron powder, the bulk boron powder being present in amorphous form;
b) compacting the bulk boron powder together with the exposed end regions of the filaments following step a) to form a compressed element; and
c) infiltrating the compressed element with molten magnesium by providing the molten magnesium in a pot and by immersing the compressed element into the molten magnesium, wherein an entire amount of the molten magnesium is introduced at a surface of the compressed element.
2. The method of claim 1 , wherein the pot is produced from a material that is inert with respect to liquid magnesium or from a material which comprises Nb, Ta, V, Ti or Fe.
3. The method of claim 1 , wherein, in step b), the compressed element is compacted to at least 40% of a theoretical density.
4. The method of claim 1 , wherein step c) is performed in a reducing atmosphere, an inert atmosphere or in an argon atmosphere.
5. The method of claim 1 , wherein the exposed end regions of different wire filaments are disposed in the bulk powder in such a fashion that they abut each other.
6. The method of claim 1 , wherein the exposed end regions of different wire filaments are disposed in the bulk powder in such a fashion that they are interwoven with each other.
7. The method of claim 1 , wherein the boron powder has a D50 grain size of ≦1 μm.
8. The method of claim 1 , wherein, in step b), the compressed element is compacted to at least 50% of a theoretical density.
9. The method of claim 1 , wherein a relative used amount n(Mg) of magnesium in the molten magnesium and n(B) of boron in the compressed element is n(Mg)/n(B)≧0.5.
10. The method of claim 9 , wherein pores of the MgB 2 matrix of the compressed element are filled with metallic magnesium.
11. A method for connecting two or more wires, each wire comprising at least one filament that contains MgB 2 or a mixture of Mg and B, wherein a superconducting connection is realized at exposed end regions of the filaments via an MgB 2 matrix the method comprising the steps of:
a) inserting the exposed end regions of the filaments into bulk boron powder, the bulk boron powder being present in amorphous form;
b) compacting the bulk boron powder together with the exposed end regions of the filaments following step a) to form a compressed element; and
c) infiltrating the compressed element with molten magnesium, wherein an entire amount of the molten magnesium is introduced at a surface of the compressed element by disposing the compressed element in a pot and by subsequently filling the pot with molten magnesium.
12. The method of claim 11 , wherein the pot is produced from a material that is inert with respect to liquid magnesium or from a material which comprises Nb, Ta, V, Ti or Fe.
13. The method of claim 11 , wherein the pot has a coating made from a material which is inert with respect to liquid magnesium or from a material which includes Nb, Ta, V, Ti or Fe.
14. A method for connecting two or more wires, each wire comprising at least one filament that contains MgB 2 or a mixture of Mg and B, wherein a superconducting connection is realized at exposed end regions of the filaments via an MgB 2 matrix, the method comprising the steps of:
a) inserting the exposed end regions of the filaments into bulk boron powder, the bulk boron powder being present in amorphous form;
b) compacting the bulk boron powder together with the exposed end regions of the filaments following step a) to form a compressed element; and
c) infiltrating the compressed element with molten magnesium, wherein an entire amount of the molten magnesium is introduced at a surface of the compressed element by completely surrounding the compressed element with the molten magnesium.
15. A method for connecting two or more wires, each wire comprising at least one filament that contains MgB 2 or a mixture of Mg and B, wherein a superconducting connection is realized at exposed end regions of the filaments via an MgB 2 matrix, the method comprising the steps of:
a) inserting the exposed end regions of the filaments into bulk boron powder, the bulk boron powder being present in amorphous form;
b) compacting the bulk boron powder together with the exposed end regions of the filaments following step a) to form a compressed element; and
c) infiltrating the compressed element with molten magnesium, wherein an entire amount of the molten magnesium is introduced at a surface of the compressed element by at least partially surrounding the compressed element with solid magnesium and heating the at least partially surrounded compressed element beyond a melting temperature of magnesium.