Solar cell using low iron high transmission glass with antimony and corresponding method
View Patent ↗A high transmission and low iron glass is provided for use in a solar cell. The glass substrate may be patterned on at least one surface thereof. Antimony (Sb) is used in the glass to improve stability of the solar performance of the glass upon exposure to ultraviolet (UV) radiation and/or sunlight. The combination of low iron content, antimony, and/or the patterning of the glass substrate results in a substrate with high visible transmission and excellent light refracting characteristics.
1. A method of making patterned glass, the method comprising:
providing a molten glass batch in a furnace or melter comprising from 67-75% SiO 2 , from about 0.01 to 0.06% total iron, and antimony oxide;
forwarding a glass ribbon from the furnace or melter to a nip between first and second rollers, at least one of the rollers having patter defined in a surface thereof, wherein the glass ribbon reaches the nip at a temperature of from about 1,900 to 2,400 degrees F.;
at the nip, transferring the pattern from the roller(s) to the glass ribbon;
the glass ribbon being at a temperature of from about 1,100 to 1,600 degrees F. upon exiting the nip;
annealing the glass ribbon at least after the ribbon exits the nip, thereby providing a patterned glass having a visible transmission of at least 90%, from about 0.01 to 0.06% total iron, and from about 0.01 to 1.0% antimony oxide, wherein the patterned glass has a glass redox of <=0.10.
2. The method of claim 1 , wherein the patterned glass has no more than 0.04% cerium oxide, a transmissive a* color value of −0.5 to +0.5 and a transmissive b* color value of from +0.1 to +1.0.
3. The method of claim 1 , wherein the patterned glass has a transmissive a* color value of −1.0 to +1.0, and a transmissive b* color value of from 0 to +1.5.
4. The method of claim 1 , wherein the patterned glass has a transmissive a* color value of −1.0 to +1.0.