Refrigerant hose
View Patent ↗An object of the present invention is to provide a hose which has a gas barrier layer and a rubber layer adhered without using an adhesive, and which has a dramatically improved durability compared to the conventional hose. The hose of the present invention is a refrigerant hose having an inner layer comprising a gas barrier layer and a rubber layer adhered to the outer surface of the gas barrier layer. The gas barrier layer comprises a modified polyamide prepared by blending a polyamide and a carboxyl group-containing modified polyolefin, and the rubber layer comprises a rubber composition prepared by blending a particular amount of an alkylphenol formaldehyde resin and a particular amount of carbon black with a raw rubber. The raw rubber comprises a BIMS, a copolymer rubber which is a butyl rubber and/or a halogenated butyl rubber, and an EPDM, the carbon black is specified, and no adhesive layer is formed between the gas barrier layer and the rubber layer.
1. A refrigerant hose having an inner layer comprising a gas barrier layer and a rubber layer adhered to an outer surface of the gas barrier layer, wherein
the gas barrier layer comprises a modified polyamide prepared by blending a polyamide and a carboxyl group-containing modified polyolefin;
the rubber layer comprises a rubber composition comprising raw rubber, alkylphenol formaldehyde resin in an amount of from 1 to 15 parts by weight based on 100 parts by weight of the raw rubber, and carbon black in an amount of from 30 to 80 parts by weight based on 100 parts by weight of the raw rubber;
wherein, based on 100 parts by weight of the raw rubber, the raw rubber comprises 5 to 40 parts by weight of a brominated product of a copolymer rubber of an isomonoolefin and a p-alkyl styrene (BIMS, 80 to 20 parts by weight of an ethylene-propylene-diene terpolymer (EPDM), and 15 to 40 parts by weight of a copolymer rubber selected from the group consisting of a butyl rubber, halogenated butyl rubber, and blends thereof; wherein
the carbon black has a value of N 2 SA of at least 75 m 2 /g as measured according to JIS K 6217-2 and a DBP absorption of at least 90 cm 3 /100 g as measured according to JIS K 6217-4; and no adhesive layer is formed between the gas barrier layer and the rubber layer.
2. The refrigerant hose according to claim 1 wherein the copolymer rubber is a halogenated butyl rubber.
3. The refrigerant hose according to claim 1 , wherein the polyamide is at least one member selected from the group consisting of polyamide 6, polyamide 11, polyamide 12, polyamide 4,6, polyamide 6,6, polyamide 6,10, polyamide 6,12, polyamide MXD-6, and a copolymer of at least two of the foregoing polyamides.
4. The refrigerant hose according to claim 2 , wherein the polyamide is at least one member selected from the group consisting of polyamide 6, polyamide 11, polyamide 12, polyamide 4,6, polyamide 6,6, polyamide 6,10, polyamide 6,12, polyamide MXD-6, and a copolymer of at least two of the foregoing polyamides.