Nonaqueous electrolyte secondary battery and method of forming positive electrode
View Patent ↗A positive electrode active material is formed of a lithium containing layered oxide. The lithium containing layered oxide contains either or both of Li A Na B Mn x Co y O 2±α that belongs to a space group P6 3 mc or Li A Na B Mn x Co y O 2±α that belongs to a space group Cmca. The lithium containing layered oxide contains the Li A Na B Mn x Co y O 2±α as a solid solution, a mixture or both of them. In the Li A Na B Mn x Co y O 2±α , 0.5≦A≦1.2, 0<B≦0.01, 0.40≦x≦0.55, 0.40≦y≦0.55, 0.80≦x+y≦1.10 and 0≦α≦0.3.
1. A nonaqueous electrolyte secondary battery comprising:
a positive electrode containing a positive electrode active material composed of a lithium containing oxide;
a negative electrode; and
a nonaqueous electrolyte, wherein
said lithium containing oxide contains Li A Na B Mn x Co y O 2±α (0.5≦A≦1.2, 0<B≦0.01, 0.40≦x≦0.55, 0.40≦y≦0.55, 0.80≦x+y≦1.10 and 0≦α≦0.3) that belongs to a space group P6 3 mc and/or a space group Cmca.
2. The nonaqueous electrolyte secondary battery according to claim 1 , wherein
said lithium containing oxide contains a substance whose diffraction angle 2θ has a peak in a range from 18.0 degrees to 19.5 degrees in an X-ray powder crystal diffraction spectrum using CuK α as an X-ray source and which belongs to a space group C2/m or a space group C2/c as a solid solution, a mixture or both of the solid solution and the mixture.
3. The nonaqueous electrolyte secondary battery according to claim 2 , wherein
said substance whose diffraction angle 2θ has the peak in the range from 18.0 degrees to 19.5 degrees is Li 1+x [Mn y Co 1-y ] 1−x O 2 (0≦x≦1/3 and 0<y≦1).
4. The nonaqueous electrolyte secondary battery according to claim 1 , wherein a real density of said lithium containing oxide is not less than 4.4 g/cm 3 .
5. The nonaqueous electrolyte secondary battery according to claim 1 , wherein
said negative electrode contains at least one selected from a group composed of lithium metal, silicon, carbon, tin, germanium, aluminum, lead, indium, gallium, a lithium containing alloy, a carbon material in which lithium is previously stored, and a silicon material in which lithium is previously stored.
6. A method of fabricating a positive electrode comprising:
forming a positive electrode active material composed of a lithium containing oxide that contains sodium by subjecting part of sodium contained in a sodium containing oxide to ion exchange for lithium, wherein
said sodium containing oxide contains Na A Li B MO 2±α (0.5≦A≦1.1, 0<B≦0.3 and 0≦α≦0.3), and said M includes at least one of manganese and cobalt, and
said sodium containing oxide contains a substance whose diffraction angle 2θ has a peak in a range from 18.0 degrees to 19.5 degrees in an X-ray powder crystal diffraction spectrum using CuK α as an X-ray source and which belongs to a space group C2/m or a space group C2/c.