Method for producing two-phase stainless steel pipe
View Patent ↗A method for producing a two-phase stainless steel pipe, which comprises: preparing a two-phase stainless steel material consisting of, by mass %, C: 0.03% or less, Si: 1% or less, Mn: 0.1 to 2%, Cr: 20 to 35%, Ni: 3 to 10%, Mo: 0 to 4%, W: 0.5 to 6%, Cu: 0 to 3% and N: more than 0.175 and up to 0.35%, and the balance being Fe and impurities; forming a material pipe by subjecting to a hot working: and performing a cold drawing, where the cold drawing is characterized in being performed under the conditions that the working ratio Rd, in terms of the reduction of area, in the final cold drawing step is within a range from 5 to 35%, and the following formula (1) is satisfied: Rd (%)≧( MYS −55)/17.2−{1.2×Cr+3.0×(Mo+0.5×W)} (1).
1. A method for producing a two-phase stainless steel pipe, which comprises,
preparing a two-phase stainless steel material having a chemical composition that consists of, by mass %, C: 0.014 to 0.03%, Si: 1% or less, Mn: 0.1 to 2%, Cr: 20 to 35%, Ni: 3 to 10%, Mo: 0 to 4%, W: 2.10 to 6%, Cu: 0 to 3% and N: more than 0.17% and up to 0.35%, and the balance being Fe and impurities;
forming a material pipe by subjecting to a hot working and
performing a cold drawing,
where the cold drawing is characterized in being performed under the conditions that the working ratio Rd, in terms of the reduction of area, in the final cold drawing step is within a range from 5 to 35%, and the following formula (1) is satisfied:
Rd (%)≧( MYS− 55)/17.2−{1.2×Cr+3.0×(Mo+0.5×W)} (1)
wherein Rd and MYS signify the working ratio (%) in terms of the reduction of area and the targeted yield strength (MPa), respectively, and Cr, Mo and W signify the contents (mass %) of the individual elements, respectively.
2. A method for producing a two-phase stainless steel pipe according to claim 1 wherein the hot working is based on the Ugine-Sejournet extrusion pipe production method.
3. A method for producing a two-phase stainless steel pipe according to claim 1 wherein the hot working is based on the Mannesmann pipe production method.