View Patent ↗Surface-modified, pyrogenically prepared silica is prepared by subjecting the pyrogenically prepared silica, which is in the form of aggregates of primary particles having a BET surface area of 300±25 m 2 /g and the aggregates have an average area of 4800-6000 nm 2 , an average equivalent circle diameter (ECD) of 60-80 nm and an average circumference of 580-750 nm, to surface-modification in a known way. It can be used as a filler for controlling the rheology of liquid silicone rubber (LSR) systems.
1. A surface-modified, pyrogenically prepared silica which is easily incorporated into liquid resin systems,
the surface modification consisting of a pyrogenic silica surface having trimethylsilyl groups;
the surface modified silica being obtained by a process comprising:
treating a pyrogenically prepared silica with a silane surface modifier consisting of hexamethyldisilazane;
wherein
the pyrogenically prepared silica comprises aggregates of primary particles having a BET surface area of 300±25 m 2 /g,
an average area of the aggregates is from 4800 to 6000 nm 2 ,
an average equivalent circle diameter (ECD) of the aggregates is from 60 to 80 nm and
an average circumference of the aggregates is from 580 to 750 nm.
2. A process for preparing the surface-modified, pyrogenically prepared silica according to claim 1 , comprising: treating a pyrogenically prepared silica with a silane surface modifier consisting of hexamethyldisilazane;
wherein
the pyrogenically prepared silica comprises aggregates of primary particles having a BET surface area of 300±25 m 2 /g,
an average area of the aggregates is from 4800 to 6000 nm 2 ,
an average equivalent circle diameter (ECD) of the aggregates is from 60 to 80 nm, and
an average circumference of the aggregates is from 580 to 750 nm.
3. The process according to claim 2 , wherein the pyrogenically prepared silica is optionally sprayed with water prior to the treatment with the hexamethyldisilazane.
4. The process according to claim 2 , wherein the hexamethyldisilazane is in vapor form for the treatment of the pyrogenically prepared silica, and
the mixture of the silica and the vapor is thermally treated at a temperature of 50 to 800° C. over a period of 0.1 to 6 h.
5. A method for controlling the rheology of a liquid system, the method comprising adding the surface modified pyrogenically prepared silica according to of claim 1 to the liquid system.
6. The method according to claim 5 , wherein the liquid system is a liquid silicone rubber (LSR) system.