Phosphorus modified molecular sieves, their use in conversion of organics to olefins
The present invention is a phosphorous modified zeolite (A) made by a process comprising in that order: selecting a zeolite with low Si/Al ratio (advantageously lower than 30) among H + or NH 4 + -form of MFI, MEL, FER, MOR, clinoptilolite, said zeolite having been made preferably without direct addition of organic template; steaming at a temperature ranging from 400 to 870° C. for 0.01-200 h; leaching with an aqueous acid solution containing the source of P at conditions effective to remove a substantial part of Al from the zeolite and to introduce at least 0.3 wt % of P; separation of the solid from the liquid; an optional washing step or an optional drying step or an optional drying step followed by a washing step; a calcination step. The present invention also relates to a process (hereunder referred as “XTO process”) for making an olefin product from an oxygen-containing, halogenide-containing or sulphur-containing organic feedstock wherein said oxygen-containing, halogenide-containing or sulphur-containing organic feedstock is contacted with the above catalyst (in the XTO reactor) under conditions effective to convert at least a portion of the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock to olefin products (the XTO reactor effluent). The present invention also relates to a process (hereunder referred as “combined XTO and OCP process”) to make light olefins from an oxygen-containing, halogenide-containing or sulphur-containing organic feedstock comprising : contacting said oxygen-containing, halogenide-containing or sulphur-containing organic feedstock in the XTO reactor with the above catalyst at conditions effective to convert at least a portion of the feedstock to form an XTO reactor effluent comprising light olefins and a heavy hydrocarbon fraction; separating said light olefins from said heavy hydrocarbon fraction; contacting said heavy hydrocarbon fraction in the OCP reactor at conditions effective to convert at least a portion of said heavy hydrocarbon fraction to light olefins.
1. A method of making a phosphorous modified zeolite, comprising:
selecting a zeolite having a Si:Al atomic ratio of 30 or less, wherein the zeolite is selected from the group consisting of MFI, MEL, FER, MOR, and clinoptilolite, and wherein the selected zeolite is in the H + or NH 4 + form;
steaming the zeolite at a temperature ranging from 400° C. to 870° C. for 0.01 h to 200 h;
leaching the zeolite with an aqueous acid solution containing a source of P at conditions effective to remove a substantial amount of Al from the zeolite and to introduce more than 0.3 wt % of P, wherein the aqueous acid solution containing the source of P comprises a salt of a phosphate ([PO 4 ] 3− ), an acid or a corresponding salt of a phosphite ([HPO 3 ] 2− ), an acid or a corresponding salt of a hypophosphite ([H 2 PO 2 ] 1− ), an acid or a corresponding salt of a diphosphate, or an acid or a corresponding salt of a polyphosphate;
separating the zeolite from the aqueous acid solution; and
calcining the zeolite.
2. The method of claim 1 , wherein the zeolite is an MFI zeolite.
3. The method of claim 1 , wherein the phosphorus modified zeolite has been made without direct addition of organic template.
4. The method of claim 1 , wherein the zeolite has an initial Si:Al atomic ratio ranging from 4 to 30.
5. The method of claim 1 , wherein the steaming step is performed at a temperature ranging from 480 to 760° C.
6. The method of claim 1 , wherein the steaming step is carried out for a period of from 0.05 to 200 hours.
7. The method of claim 6 , wherein the steaming step is carried out for a period of from 0.05 to 50 hours.
8. The method of claim 1 , wherein the step of leaching with the aqueous acid solution containing the source of P is conducted under boiling conditions of the solution.
9. The method of claim 1 , wherein the separated zeolite is subjected to a washing step or a combination of a washing step and a drying step.
10. The method of claim 9 , wherein the separated zeolite is dried at a temperature between 40 and 600° C.
11. The method of claim 1 , wherein the leaching period is 0.5 to 24 hours.
12. The method of claim 1 , wherein the aqueous acid solution containing the source of P in the leaching step has a pH of 3 or lower.
13. The method of claim 12 , wherein the aqueous leaching acid solution comprises phosphorus acids, a mixture of phosphorus acids and organic or inorganic acids, or a mixture of salts of phosphorus acids and organic or inorganic acids.
14. The method of claim 1 , wherein the final P content of the phosphorus modified zeolite is up to 7 wt %.
15. The method of claim 1 , wherein at least 10% of the Al present in the zeolite has been extracted and removed by leaching.
16. The method of claim 2 , wherein the MFI zeolite is a ZSM-5.
17. The method of claim 1 , wherein the final P content of the phosphorus modified zeolite is at least about 1.8 wt %.
18. The method of claim 17 , wherein the final P content of the phosphorus modified zeolite is up to 7 wt %.
19. The method of claim 1 , wherein the aqueous acid solution containing the source of P comprises an acid or a corresponding salt of a phosphite ([HPO 3 ] 2− ), an acid or a corresponding salt of a hypophosphite ([H 2 PO 2 ] 1− ), an acid or a corresponding salt of a diphosphate, or an acid or a corresponding salt of a polyphosphate.
20. A method of making a phosphorous modified zeolite, comprising:
selecting a zeolite having a Si:Al atomic ratio of 30 or less, wherein the zeolite is selected from the group consisting of FER, MOR, and clinoptilolite, and wherein the selected zeolite is in the H + or NH 4 + form;
steaming the zeolite at a temperature ranging from 400° C. to 870° C. for 0.01 h to 200 h;
leaching the zeolite with an aqueous acid solution containing a source of P at conditions effective to remove a substantial amount of Al from the zeolite and to introduce at least 0.3 wt % of P;
separating the zeolite from the aqueous acid solution; and
calcining the zeolite.
21. The method of claim 1 , wherein the aqueous acid solution containing the source of P comprises phosphorous acid (H 3 PO 3 ).