Process for producing reduced iron pellets, and process for producing pig iron
View Patent ↗In a method for producing a reduced iron pellet, when a powder formed article including iron oxide and carbon is heated and reduced in a rotary hearth furnace, a formed article produced using a raw material, in which an average diameter of the iron oxide is 50 microns or less and a ratio of carbon monoxide to carbon dioxide in a reduction zone is from 0.3 to 1, is reduced at a temperature of 1400° C. or less, thereby producing a reduced iron pellet in which a metallization ratio of iron is 50 to 85% and a ratio of residual carbon is 2% or less.
1. A method for producing a reduced iron pellet, the method comprising
producing the reduced iron pellet by heating and reducing a powder formed article including iron oxide and carbon in a rotary hearth furnace, wherein
a formed article, produced using a raw material in which an average diameter of the iron oxide is 25 microns or less, a ratio of carbon monoxide to carbon dioxide in a reduction zone is from 0.3 to 1, and a ratio of an atom mole amount of fixed carbon to an atom mole amount of active oxygen is 0.7 to 1.5, is reduced at a temperature of 1400° C. or less, and
a reduced iron pellet is produced in which a ratio of metallic iron to total iron is 50 to 85% and a content of residual carbon is 2% or less.
2. The method for producing a reduced iron pellet according to claim 1 , wherein
a sojourn time is within a range between a fixed lower limit of 8 minutes and a variable upper limit represented by an equation “to=69.5-0.035T”, where a unit of the variable upper limit “to” is minutes, and T is an average gas temperature (° C.) in the rotary hearth furnace within a process temperature limit between 1200° C. and 1400° C.
3. The method for producing a reduced iron pellet according to claim 1 , wherein
an average heating rate at a center of the formed article is 400° C./min or less at the time of heating from 100° C. to 1000° C.
4. The method for producing a reduced iron pellet according to claim 1 , wherein
a mass ratio of calcium oxide to silicon oxide in the formed article is 2.2 or less.
5. The method for producing a reduced iron pellet according to claim 4 , wherein
a content of halogen in the reduced iron pellet satisfies (F mass %)+0.4(Cl mass %)<0.25%.
6. The method for producing a reduced iron pellet according to claim 1 , wherein
total iron content, magnesium oxide content, calcium oxide content and silicon oxide content in the formed article satisfies {(CaO mass %)−(MgO mass %)}/(total iron mass %)<0.1 and {(CaO mass %)−(MgO mass %)/(SiO 2 mass %)<2.0.
7. A method for producing pig iron, wherein
a reduced iron pellet produced by heating a powder formed article including iron oxide and carbon in a rotary hearth furnace at a temperature of 1250 to 1400° C. under a condition wherein a ratio of carbon monoxide to carbon dioxide in a reduction zone is from 0.55 to 1, in which a content of total iron is 55 mass % or more, a ratio of metallic iron to total iron is 50 to 85%, particles of metal iron with an average of 35 microns or less are coupled to each other to form a metal iron network between the iron oxide and a mixture of other oxides, a porosity is 20 to 50%, and a content of a residual carbon is 2% or less,
is fed into an iron producing blast furnace together with ore and sintered ore in a condition that a ratio of the reduced iron pellet having a size of 5 to 20 mm to a total mass of the reduced iron pellet is 80% or more, and the fed pellet is reduced and melted.
8. The method for producing pig iron according to claim 7 , wherein
the reduced iron pellet having an inner structure, in which an average diameter of oxide including the iron oxide is 5 to 100 micron and the iron oxide is restricted by the metal iron network, is fed into an iron producing blast furnace together with ore and sintered ore, and is reduced and melted.
9. The method for producing pig iron according to claim 7 , wherein
the reduced iron pellet is fed into the iron producing blast furnace at a ratio of 250 kg/metric ton or less with respect to an amount of produced pig iron.
10. The method for producing pig iron according to claim 7 , wherein
the reduced iron pellet is fed into a position within ⅔ from the center in a diameter direction of the iron producing furnace, so that a ratio of reduced iron pellets to a total charge of materials in the iron producing blast furnace is 65% or more.
11. A method for producing pig iron, the method comprising
producing the pig iron by heating a powder formed article including iron oxide and carbon in a rotary hearth furnace, wherein
the reduced iron pellet produced by the method according to claim 1 in which a content of total iron is 55 mass % or more, a ratio of metallic iron to total iron is 50 to 85%, and a porosity is 20 to 50%,
is fed into an iron producing blast furnace together with ore and sintered ore in a condition that a ratio of the reduced iron pellet having a size of 5 to 20 mm to a total mass of the reduced iron pellet is 80% or more, and the fed pellet is reduced and melted.
12. A method for producing pig iron, wherein
a reduced iron pellet produced by heating a powder formed article including iron oxide and carbon in a rotary hearth furnace at a temperature of 1250 to 1400° C. under a condition wherein a ratio of carbon monoxide to carbon dioxide in a reduction zone is from 0.55 to 1, in which a content of total iron is 55 mass % or more, a ratio of metallic iron to total iron is 50 to 85%, particles of metal iron with an average of 35 microns or less are coupled to each other to form a metal iron network between the iron oxide and a mixture of other oxides, a porosity is 20 to 50%, and a content of a residual carbon is 2% or less,
is fed into a vertical furnace, in which an in-furnace space filling ratio of iron chunks and coke chunks is 80% or less, in a condition that a ratio of the reduced iron pellet having a size of 5 to 20 mm to a total mass of the reduced iron pellet is 80% or more, and the fed iron pellet is reduced and melted.
13. The method for producing pig iron according to claim 12 , wherein
the reduced iron pellet is reduced and melted in a condition that a ratio of the reduced iron pellet to the iron chunks in the vertical furnace is 100% or less.
14. The method for producing pig iron according to claim 12 , wherein
the reduced iron pellet is fed into a position within ⅔ from the center in a diameter direction of the vertical furnace, so that a ratio of reduced iron pellets to a total charge of materials in the vertical furnace is 70% or more.
15. The method for producing pig iron according to claim 12 , wherein
a reduced iron pellet produced by heating a powder formed article including at least one of zinc and lead, iron oxide, and carbon in a rotary hearth furnace, in which a total content of zinc and lead is 0.05% or more,
is fed into the vertical furnace in which a gas temperature of an upper part of the furnace is 500° C. or more, and is reduced and melted.
16. A method for producing pig iron, the method comprising
producing the pig iron by heating a powder formed article including iron oxide and carbon in a rotary hearth furnace, wherein
the reduced iron pellet produced by the method according to claim 1 in which a content of total iron is 55 mass % or more, a ratio of metallic iron to total iron is 50 to 85%, a metal iron network is formed between the iron oxide and a mixture of other oxides, and a porosity is 20 to 50%,
is fed into a vertical furnace, in which an in-furnace space filling ratio of iron chunks and coke chunks is 80% or less, in a condition that a ratio of the reduced iron pellet having a size of 5 to 20 mm to a total mass of the reduced iron pellet is 80% or more, and the fed reduced iron pellet is reduced and melted.