Reinforced and conductive resin compositions comprising polyolefins and poly(hydroxy carboxylic acid)

1. A process for preparing a resin composition comprising:

blending a poly(hydroxy carboxylic acid) with carbon nanotubes to form a composite, wherein the blending of the poly(hydroxy carboxylic acid) with the carbon nanotubes comprises solution processing, dry blending, dry blending and melt blending, or melt blending; and

blending the composite with a polyolefin to form the resin composition.

2. The process of claim 1 , wherein the polyolefin was prepared with a single-site catalyst.

3. The process of claim 1 , wherein the poly(hydroxy carboxylic acid) is polylactic acid.

4. The process of claim 1 , wherein the poly(hydroxy carboxylic acid) is melt blended with carbon nanotubes.

5. A resin composition comprising a polyolefin and a composite comprising carbon nanotubes and poly(hydroxy carboxylic acid), wherein the poly(hydroxy carboxylic acid) and the carbon nanotubes are blended via solution processing, dry blending, dry blending and melt blending, or melt blending.

6. The resin composition of claim 5 , wherein the polyolefin was prepared with a single-site catalyst.

7. The resin composition of claim 5 , wherein the poly(hydroxy carboxylic acid) is polylactic acid.

8. The resin composition of claim 5 , wherein the resin composition comprises at most 10% by weight of carbon nanotubes based on a total weight of the resin composition.

9. The resin composition of claim 5 , wherein the polyolefin is selected from polypropylene and polyethylene homo- and copolymers.

10. The resin composition of claim 5 , wherein the carbon nanotubes and the poly(hydroxy carboxylic acid) are blended to form the composite prior to blending the composite with the polyolefin.

11. The resin composition of claim 5 , wherein the carbon nanotubes are single walled carbon nanotubes having:

a diameter of at least 0.5 nanometers and at most 50 nanometers;

a length of at least 1 microns and at most 5 centimeters; and

a length/diameter aspect ratio of at least 100.

12. The resin composition of claim 5 , wherein the carbon nanotubes are multi-walled carbon nanotubes having:

a diameter of at least 2 nanometers and at most 100 nanometers;

a length of at least 1 micron and at most 100 microns; and

a length/diameter aspect ratio of at least 100.

13. The resin composition of claim 5 , wherein the carbon nanotubes are non-functionalised carbon nanotubes.

14. The resin composition of claim 5 , wherein the resin composition comprises from 1 to 50 wt % of the composite.

15. The resin composition of claim 5 , wherein the resin composition comprises from 1 to 99 wt % of the polyolefin.

16. The resin composition of claim 5 , wherein the composite comprises up to 99 wt % of the carbon nanotubes and from 1 wt % to 99 wt % of the poly(hydroxy carboxylic acid).

17. The process of claim 1 , wherein the polyolefin is melt blended with the composite.

18. The process of claim 1 , wherein the formed composite is a homogenous composite comprising the carbon nanotubes dispersed in a matrix of the poly(hydroxy carboxylic acid); and

wherein the formed resin composition is a homogenous blend of the polyolefin and the poly(hydroxy carboxylic acid) with the carbon nanotubes dispersed throughout the homogenous blend.

19. A process for preparing a resin composition comprising:

polymerizing hydroxy carboxylic acid monomers to form poly(hydroxy carboxylic acid);

blending the poly(hydroxy carboxylic acid) with carbon nanotubes to form a composite; and

blending the composite with a polyolefin to form the resin composition, wherein the composite comprises the carbon nanotubes dispersed within the poly(hydroxy carboxylic acid).

20. The process of claim 19 , wherein the blending of the poly(hydroxy carboxylic acid) with the carbon nanotubes comprises solution processing, dry blending, dry blending and melt blending, or melt blending.