Use of a polyamide molding compound for lining conduits
View Patent ↗In a method for the introduction of an inliner into a pipe or a pipeline, where the external diameter of the inliner is greater than the internal diameter of the pipe or of the pipeline, and where the action of an external force is used to reduce the cross section of the inliner prior to the introduction, the inliner is composed of a polyamide moulding composition which comprises at least 50% by weight of polyamide which is not PA11. The recovery behavior of said polyamides is similar to that of polyethylene usually used for this purpose.
1. A method comprising introducing an inliner into a pipe or a pipeline, wherein an external diameter of the inliner is greater than an internal diameter of the pipe or of the pipeline; an external force reduces a cross section of the inliner prior to the introduction; and
the inliner comprises a polyamide moulding composition which comprises at least 50% by weight of polyamide selected from the group consisting of PA610, PA612, PA613, PA1010, PA1012, PA1014, PA12, PA1212 and materials based thereon which are polyetheresteramides or which are polyetheramides.
2. The method according to claim 1 , wherein the cross section of the inliner is reduced by at least 3%.
3. The method according to a claim 1 , wherein
the polyamide of the polyamide moulding composition comprises from 1 to 70% by weight of at least one of polyetheresteramide and polyetheramide.
4. The method according to claim 1 , wherein
the polyamide moulding composition comprises from 1 to 25% by weight of plasticizer.
5. The method according to claim 1 , comprising
producing the inliner by a method comprising condensing the polyamide of the moulding composition to have a higher molecular weight through addition of a compound having at least two carbonate units in a quantitative ratio of from 0.005 to 10% by weight, based on the polyamide, wherein
a) a starting polyamide moulding composition is provided,
b) a premix of the starting polyamide composition and of the compound having at least two carbonate units is prepared,
c) the premix is, optionally stored, and
d) the premix is then processed to give the moulding, and the condensation to give a higher molecular weight is carried out.
6. A pipeline which comprises an inliner introduced by the method according to claim 1 .
7. A transport comprising a pipeline according to claim 6 .
8. The method according to claim 1 , wherein the external diameter of said inliner is at most 10% of said internal diameter of said pipe or of said pipeline.
9. The method according to claim 1 , wherein the cross section of the inliner is reduced by at least 4%.
10. The method according to claim 1 , wherein the cross section of the inliner is reduced by at least 5%.
11. The method according to claim 1 , wherein the cross section of the inliner is reduced by at least 6%.
12. The method according to claim 1 , wherein the cross section of the inliner is reduced by at least 7%.
13. The method according to claim 1 , wherein the said polyamide moulding composition comprises at least 60% by weight of said polyamide.
14. The method according to claim 1 , wherein the said polyamide moulding composition comprises at least 70% by weight of said polyamide.
15. The method according to claim 1 , wherein the said polyamide moulding composition comprises at least 80% by weight of said polyamide.
16. The method according to claim 5 , wherein the said compound having at least two carbonate units is used in a quantitative ratio of from 0.01 to 5.0 wt. %.
17. The method according to claim 5 , wherein the said compound having at least two carbonate units is used in a quantitative ratio of from 0.05 to 3 wt. %.