Electrolytic manganese dioxide for lithium primary battery, manufacturing method therefor, and lithium primary battery using same
View Patent ↗Electrolytic manganese dioxide for lithium primary batteries has a sodium content of 0.05 to 0.2% by mass, and a pH of 5 to 7 as measured according to JIS-K-1467. Using this electrolytic manganese dioxide as a positive electrode active material for lithium primary batteries enables the batteries to be excellent in both initial discharge characteristics and long-term discharge characteristics.
1. A method for producing electrolytic manganese dioxide for lithium primary batteries, the method comprising:
preparing neutralized electrolytic manganese dioxide by neutralizing electrolytic manganese dioxide with sodium hydroxide, the electrolytic manganese dioxide being electrosynthesized in an acid electrolytic bath; and
washing the neutralized electrolytic manganese dioxide with water and drying the washed neutralized electrolytic manganese dioxide to prepare water-washed electrolytic manganese dioxide having a sodium content of 0.05 to 0.2% by mass, and a pH of 5 to 7 as measured according to JIS-K-1467, wherein an amount of water in the washing the neutralized electrolytic manganese dioxide is adjusted so that the water-washed electrolytic manganese dioxide after drying has a pH of 5 to 7 as measured according to JIS-K-1467.
2. The method of claim 1 , wherein
the neutralized electrolytic manganese dioxide before washing has a sodium content of 0.1 to 0.4% by mass.
3. The method of claim 1 , further comprising:
drying the neutralized electrolytic manganese dioxide before washing,
wherein the dried neutralized electrolytic manganese dioxide is washed when preparing the water-washed electrolytic manganese dioxide.
4. The method of claim 3 , wherein
the dried neutralized electrolytic manganese dioxide before washing has a sodium content of 0.1 to 0.4% by mass.
5. The method of claim 1 , wherein the amount of water is 5 kg to 40 kg per 1 kg of the neutralized electrolytic manganese dioxide.
6. The method of claim 3 , wherein an amount of water in washing the dried neutralized electrolytic manganese dioxide is adjusted so that the water-washed electrolytic manganese dioxide after drying has a pH of 5 to 7 as measured according to JIS-K-1467.
7. The method of claim 3 , wherein the amount of water is 5 kg to 40 kg per 1 kg of the dried neutralized electrolytic manganese dioxide.
8. The method of claim 4 , wherein an amount of water in washing the dried neutralized electrolytic manganese dioxide is adjusted so that the water-washed electrolytic manganese dioxide after drying has a pH of 5 to 7 as measured according to JIS-K-1467.
9. The method of claim 4 , wherein the amount of water is 5 kg to 40 kg per 1 kg of the dried neutralized electrolytic manganese dioxide.