Secondary battery with improved storage characteristics and method for manufacturing the same
View Patent ↗Provided is a secondary battery comprising a separator having an inorganic layer wherein active sites of inorganic particles in the inorganic layer are modified into non-reactive sites. Use of the separator leads to improvements in wettability of an electrolyte and thermoelectric stability and storage characteristics of the secondary battery. Provided is also a method of manufacturing the same secondary battery.
1. A secondary battery comprising an electrode, an electrolyte, and a separator,
wherein the separator is an organic/inorganic composite separator comprising:
an organic layer selected from the group consisting of a polyethylene layer, a polypropylene layer, a polyethylene/polypropylene bilayer, a polyethylene/polypropylene/polyethylene trilayer, a polypropylene/polyethylene/polypropylene trilayer, and an organic fiber filter paper layer; and
an inorganic layer comprising inorganic particles and an inorganic modifying agent,
wherein the inorganic particles comprise an OH group and at least one selected from the group consisting of alumina, titanium oxide, zirconium oxide, zinc oxide, silicon dioxide, and magnesium oxide;
the inorganic modifying agent comprises at least one functional group selected from the group consisting of phosphonate, phosphate, and phosphonic acid; and
a molar ratio of the OH group of the inorganic particles and the functional group of the inorganic modifying agent is from 5:1 to 10:1.
2. The secondary battery according to claim 1 , wherein the inorganic modifying agent comprises at least one selected form the group consisting of phenyl phosphonic acid, methyl phosphonic acid, triphenyl phosphate, and diethylmethyl phosphonate.
3. The secondary battery according to claim 1 , wherein the inorganic layer is formed on at least a surface of the organic layer by preparing slurry containing the inorganic particles, the inorganic modifying agent, a solvent, and a resin, and coating the surface of the organic layer with the slurry.
4. The secondary battery according to claim 3 , wherein the slurry is prepared by stirring the inorganic particles and the inorganic modifying agent in the solvent to modify the inorganic particles and then mixing the modified inorganic particles and the solvent with resin.
5. A method for manufacturing a secondary battery comprising an organic/inorganic composite separator, the method comprising the steps of:
preparing slurry comprising 1 wt % to 20 wt % of an inorganic modifying agent, inorganic particles, a solvent, and a resin, wherein the inorganic modifying agent comprises at least one functional group selected from the group consisting of phosphonate, phosphate, and phosphonic acid, and the inorganic particles comprise at least one selected from the group consisting of alumina, titanium oxide, zirconium oxide, zinc oxide, silicon dioxide, and magnesium oxide; and
forming an inorganic layer by coating at least a surface of an organic layer with the slurry, wherein the organic layer is a layer selected from the group consisting of a polyethylene layer, a polypropylene layer, a polyethylene/polypropylene bilayer, a polyethylene/polypropylene/polyethylene trilayer, a polypropylene/polyethylene/polypropylene trilayer, and an organic fiber filter paper layer.
6. The method according to claim 5 , wherein the inorganic modifying agent comprises at least one selected from the group consisting of phenyl phosphonic acid, methyl phosphonic acid, triphenyl phosphate, and diethylmethyl phosphonate.
7. The method according to claim 5 , wherein the step of preparing slurry comprises the steps of:
modifying the inorganic particles by stirring a solution containing the inorganic modifying agent and the inorganic particles until a molar ratio of the functional group of the inorganic modifying agent and an OH group included in the inorganic particles becomes 1:5 to 1:10; and
mixing the resin to the solution containing the modifying inorganic particles.