Catalyst for the hydrogenation of unsaturated hydrocarbons and process for its preparation
View Patent ↗The present invention relates to a catalyst for the hydrogenation of unsaturated hydrocarbons, in particular aromatics with a broad molecular weight range, a process for the production thereof and a process for hydrogenating unsaturated hydrocarbons.
1. A catalyst for the hydrogenation of unsaturated hydrocarbons, which catalyst is a supported nickel on silica catalyst, has a nickel content of 40 to 85 weight-% (calculated as NiO), a silicon content of 15 to 60 weight-% (calculated as SiO 2 ), a titanium content of 0.5 to 5.0 weight-% (calculated as TiO 2 ), and does not contain more than 0.20 weight-% iron (calculated as Fe), wherein the catalyst has a monomodal Ni-crystallite size distribution with a mean crystallite size of the reduced catalyst of 1.5 to 3.5 nm, a pore volume of at least 0.60 ml/g and wherein the proportion of the pore volume of pores with a pore diameter of ≧10 nm is at least 55%.
2. A catalyst as claimed in claim 1 , wherein the reduction level of nickel in the catalyst is from 52 to 80%.
3. A catalyst as claimed in claim 1 , which has an aluminum content of 2 to 10 weight-% (calculated as Al 2 O 3 ).
4. A catalyst as claimed in claim 1 , which has a magnesium content of 0.1 to 3.0 weight-% (calculated as MgO).
5. A catalyst as claimed in claim 1 , which has a zinc content of 0.1 to 4.0 weight-% (calculated as ZnO).
6. A catalyst as claimed in claim 1 , which has a chromium content of 0.1 to 0.3 weight-% (calculated as Cr 2 O 3 ).
7. A catalyst as claimed in claim 1 , which has a zirconium content of 0.1 to 3.0 weight-% (calculated as ZrO 2 ).
8. A catalyst as claimed in claim 1 , which is a powdered catalyst whose pore volume is at least 0.68 ml/g, or which is a shaped catalyst wherein the proportion of the pore volume of pores with a pore diameter ≧10 nm is at least 65%.
9. A catalyst as claimed in claim 1 , wherein the support contains one or more of the compounds selected from the group consisting of magnesium silicate, aluminosilicate, TiO 2 , nickel titanate, zirconium dioxide, nickel zirconate and ZnO.