Method for producing alkali-free glass
View Patent ↗To provide a method whereby it is possible to produce an alkali-free glass having little bubbles therein and excellent in homogeneity and flatness. A method for producing an alkali-free glass, which comprises melting a glass raw material containing a silicon source, followed by forming, wherein as the silicon source, a silica sand is used which has a median particle diameter D 50 of from 20 μm to 80 μm and which contains particles having a particle diameter of at most 2 μm at a ratio of at most 0.3 vol % and particles having a particle diameter of at least 100 μm at a ratio of at most 2.5 vol %.
1. A method for producing an alkali-free glass, which comprises
melting a glass raw material containing a silicon source, followed by forming,
wherein as the silicon source, a silica sand is used which has a median particle diameter D 50 of 18 to 27 μm, and which contains primary particles having a particle diameter of at most 2 μm at a ratio of at most 0.3 vol % and particles having a particle diameter of at least 100 μm at a ratio of at most 2.5 vol %, and
wherein the glass raw material contains, as a boron source, boric acid anhydride in an amount of from 10 to 100 mass % per 100 mass % (as calculated as B 2 O 3 ) of the boron source.
2. The method for producing an alkali-free glass according to claim 1 , wherein the ratio of the primary particles having a particle diameter of at most 2 μm is 0 vol %.
3. The method for producing an alkali-free glass according to claim 1 , wherein the glass raw material is a glass raw material which becomes an alkali-free glass having the following composition (1) as represented by mass percentage based on oxides:
SiO 2 : 50 to 66 mass %, Al 2 O 3 : 10.5 to 22 mass %, B 2 O 3 : 5 to 12 mass %, MgO: 0 to 8 mass %, CaO: 0 to 14.5 mass %, SrO: 0 to 24 mass %, BaO: 0 to 13.5 mass %, and MgO+CaO+SrO+BaO: 9 to 29.5 mass % (1).
4. The method of claim 3 , wherein the forming forms a silica glass having a ΔSiO 2 of less than 2.1 mass %.
5. The method of claim 3 , wherein the forming forms a silica glass having a ΔSiO 2 of at most 2.0 mass %.
6. The method for producing an alkali-free glass according to claim 1 , wherein the glass raw material is a glass raw material which becomes an alkali-free glass having the following composition (2) as represented by mass percentage based on oxides:
SiO 2 : 58 to 66 mass %, Al 2 O 3 : 15 to 22 mass %, B 2 O 3 : 5 to 12 mass %, MgO: 0 to 8 mass %, CaO: 0 to 9 mass %, SrO: 3 to 12.5 mass %, BaO: 0 to 2 mass %, and MgO+CaO+SrO+BaO: 9 to 18 mass % (2).
7. The method for producing an alkali-free glass according to claim 1 , wherein the glass raw material is a glass raw material which becomes an alkali-free glass having the following composition (3) as represented by mass percentage based on oxides:
SiO 2 : 50 to 61.5 mass %, Al 2 O 3 : 10.5 to 18 mass %, B 2 O 3 : 7 to 10 mass %, MgO: 2 to 5 mass %, CaO: 0 to 14.5 mass %, SrO: 0 to 24 mass %, BaO: 0 to 13.5 mass %, and MgO+CaO+SrO+BaO: 16 to 29.5 mass % (3).
8. The method of claim 1 , wherein the median particle diameter D 50 of the silica sand is 25 μm to 27 μm.
9. The method of claim 1 , wherein the median particle diameter D 50 of the silica sand is 23 μm to 27 μm.
10. The method of claim 1 , wherein the forming forms a silica glass having less than 3.1 ×10 5 bubbles/kg.
11. The method of claim 1 , wherein the forming forms a silica glass having at most 3 ×10 5 bubbles/kg.
12. The method of claim 1 , wherein the glass raw material contains boric acid anhydride in an amount of 20 to 100 mass % per 100 mass % of the boron source.
13. The method of claim 1 , wherein the glass raw material contains boric acid anhydride in an amount of from 40 to 100 mass % per 100 mass % of the boron source.
14. The method of claim 1 , wherein the forming includes a degassing step.
15. The method of claim 1 , wherein the forming forms a boron-comprising silicon glass comprising 59-60 mass % of SiO 2 , 17-18 mass % A 1 2 O 3 , 3-5 mass % of MgO, 4-6 mass % of CaO and 4-8 mass % of SrO.
16. A glass substrate made by the method of claim 1 .
17. The method of claim 1 , wherein the median particle diameter D 50 of the silica sand is from 20 to 27 μm.
18. The method of claim 1 , wherein the silica sand contains primary particles having a particle diameter of at most 2 μm at a ratio of 0%.