Mold for producing silica crucible
In a mold for use in the production of a silica crucible, a mold cover corresponding to a small-diameter thinned portion of an upper part of the silica crucible is detachably disposed on a mold substrate corresponding to a main body of the silica crucible, and the mold cover has a barrier function against arc heating, and an inner diameter of the mold cover is smaller than that of the mold substrate but larger than that of the silica crucible.
1. A mold for use in the production of a silica crucible, comprising:
a mold substrate having a shape corresponding to a main body of a silica crucible to be formed in the mold;
a mold cover having a shape corresponding to a shape of a small-diameter thinned portion of an upper part of the silica crucible to be formed in the mold, wherein the mold cover is detachably disposed on the mold substrate, and the mold cover has a barrier function against arc heating, and an inner diameter of the mold cover is smaller than an inner diameter of the mold substrate but larger than an inner diameter of the silica crucible to be formed in the mold.
2. A mold for use in the production of a silica crucible according to claim 1 , wherein a protruding thickness t 1 of an inner surface of the mold cover from an inner surface of the mold substrate, which is defined by t 1 =(inner diameter of mold substrate−inner diameter of mold cover)/2, is 20 to 80% of a thickness t 2 of silica or quartz powder attached to the inner surface of the mold substrate.
3. A mold for use in the production of a silica crucible according to claim 1 , wherein an outer diameter of the mold cover is smaller than an outer diameter of the mold substrate.
4. A mold for use in the production of a silica crucible according to claim 1 , wherein the mold cover is of onepiece-type or split-type.
5. A mold for use in the production of a silica crucible according to claim 1 , wherein the mold is used in a rotating mold method.
6. A method for making a crucible, comprising:
providing a mold with a substrate in a shape corresponding to a main body of a crucible to be formed in the mold;
providing a mold cover detachably disposed on the mold substrate;
providing quartz or silica powder in the mold;
rotating the mold; and
fusing the silica or quartz powder attached onto an inner wall of the mold through arc heating to provide a formed crucible, wherein the mold cover has a shape corresponding to a shape of a small-diameter thinned portion of an upper part of the formed crucible, and the mold cover has a barrier function against arc heating, and an inner diameter of the mold cover is smaller than an inner diameter of the mold substrate but larger than an inner diameter of the crucible.