Polyurethane compositions for golf balls
View Patent ↗A method of forming golf balls with at least a portion formed from polyurethane and polyurea compositions employing a curative blend that includes a pigment, a curing agent, and a compatible freezing point depressing agent so that the curative blend has a lower freezing point than the curing agent by itself and the blend does not lose pigment dispersion upon solidification and subsequent thawing.
1. A method of forming a golf ball comprising the steps of:
providing a curative blend formed from a saturated curing agent, a compatible saturated freezing point depressing agent, and a grind vehicle comprising a pigment, wherein the saturated curing agent has a first freezing point and the curative blend has a second freezing point less than the first freezing point;
forming a composition comprising:
a prepolymer formed from the reaction product of a saturated isocyanate and a saturated polyol or saturated polyamine; and
the curative blend; and
forming at least a portion of the golf ball from the composition.
2. The method of claim 1 , wherein the step of forming at least a portion of the golf ball comprises providing a core and forming a cover from the composition disposed about the core.
3. The method of claim 1 , wherein the second freezing point is less than the first freezing point by about 5° F. or greater.
4. The method of claim 3 , wherein the second freezing point is less than the first freezing point by about 10° F. or greater.
5. The method of claim 1 , wherein the step of providing a curative blend comprises selecting a freezing point depressing agent having a freezing point from about −10° F. to about −100° F.
6. The method of claim 1 , wherein the step of providing a curative blend comprises selecting a freezing point depressing agent comprising hydroxy-terminated freezing point depressing agents selected from the group consisting of 1,3-propanediol, 2-methyl-1,3-propanediol, 2-methyl-1,4-butanediol, 1,2-butanediol, 1,3-butanediol, ethylene glycol, diethylene glycol, 1,5-pentanediol, polytetramethylene glycol, propylene glycol, or mixtures there of.
7. The method of claim 1 , wherein the freezing point depressing agent has a freezing point of about 10° F. or less.
8. A method of forming a golf ball comprising:
providing a core;
forming a composition comprising:
a saturated prepolymer formed from the reaction product of a saturated isocyanate and a saturated polyol, saturated polyamine, or a mixture thereof; and
a curative blend formed from a saturated curing agent, a compatible saturated freezing point depressing agent present in an amount of about 8 percent or greater by weight of the curative blend, and a pigment dispersed in a grind vehicle; and
forming a layer from the composition about the core.
9. The method of claim 8 , wherein the saturated freezing point depressing agent has a freezing point of about −10° F. to about −120° F.
10. The method of claim 8 , wherein the saturated curing agent has a first freezing point and the curative blend has a second freezing point that is less than the first freezing point by about 5° F. or greater.
11. The method of claim 10 , wherein the saturated curing agent has a first freezing point and the curative blend has a second freezing point that is less than the first freezing point by about 10° F. or greater.
12. The method of claim 8 , wherein the saturated freezing point depressing agent is present in an amount of about 10 percent or greater by weight of the curative blend.
13. A method of forming a golf ball comprising the steps of:
providing a core;
providing a curative blend formed from a curing agent, a compatible freezing point depressing agent, and a pigment dispersed in a grind vehicle;
forming a composition comprising:
a prepolymer formed from the reaction product of a isocyanate and a polyol or polyamine; and
the curative blend; and
casting a cover from the composition about the core, wherein the cover has a thickness of from about 0.02 inches to about 0.035 inches.
14. The method of claim 13 , wherein the step of providing a curative blend comprises selecting a freezing point depressing agent from the group consisting of 1,3-propanediol, 2-methyl-1,3-propanediol, 2-methyl-1,4-butanediol, 1,2-butanediol, 1,3-butanediol, ethylene glycol, diethylene glycol, 1,5-pentanediol, polytetramethylene glycol, propylene glycol, and mixtures thereof.
15. The method of claim 13 , wherein the step of providing a curative blend comprises selecting a freezing point depressing agent having a freezing point from about −10° F. to about −100° F.
16. The method of claim 13 , wherein the curing agent has a first freezing point and the curative blend has a second freezing point that is less than the first freezing point by about 5° F. or greater.
17. The method of claim 16 , wherein the second freezing point is less than the first freezing point by about b 10 ° F. or greater.
18. The method of claim 13 , wherein the curative blend has a freezing point of about −30° F. to about −70° F.