Composition for stripping color filter and regeneration method of color filter using the same
View Patent ↗A composition for stripping a color filter and a color filter regeneration method are provided. A composition for stripping the color filter according to an exemplary embodiment of the present invention includes glycol and potassium hydroxide (KOH), in which either (a) the concentration of the glycol is in the range of 83 wt % to 91 wt % and of the concentration of the potassium hydroxide satisfies the condition: (wt % of KOH)≧6−(0.065*(wt % of the glycol)), or (b) the concentration of glycol is more than 91 wt % and the concentration of potassium hydroxide (KOH) is more than 0.2 wt %.
1. A method for regenerating a color filter comprising:
forming a partition on a substrate;
forming a first color filter filling within the partition; and
removing the first color filter with a composition for stripping a color filter including glycol and potassium hydroxide (KOH),
wherein either (a) the concentration of the glycol is in the range of 83 wt % to 91 wt % and the concentration of the potassium hydroxide satisfies the condition (wt % of KOH)≧6−(0.065*(wt % of the glycol)), or (b) the concentration of glycol is more than 91 wt % and the concentration of potassium hydroxide (KOH) is more than 0.2 wt %.
2. The method of claim 1 , wherein
the first color filter is removed at a temperature in the range of 20 degrees Celsius to 30 degrees Celsius.
3. The method of claim 2 , wherein
the composition for stripping the color filter is manufactured at a temperature in the range of 20 degrees Celsius to 30 degrees Celsius.
4. The method of claim 3 , further comprising
after forming the first color filter, executing natural drying or baking at a temperature of less than 150 degrees Celsius.
5. The method of claim 4 , wherein
the first color filter is formed through an Inkjet printing method after forming the partition.
6. The method of claim 5 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
7. The method of claim 6 , further comprising
plasma-treating the partition before forming the second color filter.
8. The method of claim 7 , further comprising
plasma-treating the partition after forming the partition.
9. The method of claim 8 , wherein
the partition functions as a light blocking member.
10. The method of claim 8 , wherein
the partition is an organic layer or a transparent organic layer.
11. The method of claim 2 , further comprising
after forming the first color filter, executing natural drying or baking at a temperature of less than 150 degrees Celsius.
12. The method of claim 2 , wherein
the first color filter is formed through an Inkjet printing method after forming the partition.
13. The method of claim 12 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
14. The method of claim 13 , further comprising
plasma-treating the partition before forming the second color filter.
15. The method of claim 2 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
16. The method of claim 15 , further comprising
plasma-treating the partition before forming the second color filter.
17. The method of claim 1 , wherein
the composition for stripping the color filter is manufactured at a temperature in the range of 20 degrees Celsius to 30 degrees Celsius.
18. The method of claim 17 , wherein
the first color filter is formed through an Inkjet printing method after forming the partition.
19. The method of claim 18 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
20. The method of claim 19 , further comprising
plasma-treating the partition before forming the second color filter.
21. The method of claim 1 , further comprising
after forming the first color filter, executing natural drying or baking at a temperature of less than 150 degrees Celsius.
22. The method of claim 1 , wherein
the first color filter is formed through an Inkjet printing method after forming the partition.
23. The method of claim 22 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
24. The method of claim 23 , further comprising
plasma-treating the partition before forming the second color filter.
25. The method of claim 1 , further comprising
forming a second color filter within the partition by using the Inkjet printing method without the removal of the partition after removing the first color filter.
26. The method of claim 25 , further comprising
plasma-treating the partition before forming the second color filter.