Methods for fabricating analytical substrates using metallic nanoparticles
An analytical substrate for amplifying Raman signals by a factor greater than 10,000, or by a factor less than 1,000,000. The analytical substrate is fabricated by depositing a film on the substrate and heating the substrate to a temperature less than 100 degrees Celsius for a period of time less than 30 seconds. The film can comprise a metallic nanoparticle dispersion that can further comprise a population of metallic nanoparticles. In some instances, the metallic nanoparticles have an average cross-sectional dimension in a range of about 1 nm to about 100 nm. In other instances each nanoparticle comprises at least one ligand bound to a surface of the nanoparticle, where the ligand comprises a heteroatom head group bound to the nanoparticle surface and a tail bound to the heteroatom head group.
1. A method for fabricating a substrate that amplifies Raman signals, the method comprising:
depositing, on a substrate, a film comprising a metallic nanoparticle dispersion that comprises a metallic nanoparticle population; and
heating the substrate to a temperature less than 100 degrees Celsius for a period of time less than 30 seconds to generate a substrate for amplifying a Raman signal by a factor greater than 10,000.
2. The method of claim 1 , wherein depositing the film further comprises depositing the film comprising metallic nanoparticles having an average cross-sectional dimension in a range of about 1 nm to about 100 nm.
3. The method of claim 1 , wherein depositing the film further comprises depositing the film comprising metallic nanoparticles wherein each nanoparticle comprises at least one ligand bound to a surface of the nanoparticle, the ligand comprising a heteroatom head group bound to the nanoparticle surface and a tail bound to the heteroatom head group.
4. The method of claim 1 , wherein heating the substrate further comprises heating the to generate a substrate for amplifying the Raman signal by a factor less than 1,000,000.
5. The method of claim 1 , wherein heating the substrate further comprises heating the substrate to a temperature less than 80 degrees Celsius.
6. The method of claim 1 , wherein heating further comprises heating the substrate to generate a substrate comprising a network of metallic nanoparticle structures that further comprise hot spots.
7. The method of claim 1 , wherein heating the substrate further comprises heating the substrate to a temperature less than 50 degrees Celsius.
8. The method of claim 1 , wherein depositing on a substrate further comprises depositing on a substrate comprising paper.
9. The method of claim 1 , wherein heating the substrate further comprises heating the substrate for a period of time less than 15 seconds.
10. The method of claim 1 , further comprising heating the substrate at a temperature less than 100 degrees Celsius for a period of time less than 30 seconds to generate a substrate comprising a metallic nanoparticle structure comprising an optimum interparticle spacing.
11. An analytical substrate that amplifies Raman signals, the analytical substrate comprising:
a substrate; and
at least one metallic nanoparticle structure fabricated by:
depositing on the substrate a metallic nanoparticle dispersion comprising a metallic nanoparticle population, and
heating the substrate to a temperature less than 100 degrees Celsius for a period of time less than 30 seconds, wherein the at least one metallic nanoparticle structure amplifies a Raman signal by a factor greater than 10,000.
12. The analytical substrate of claim 11 , wherein each metallic nanoparticle of the metallic nanoparticle population comprises an average cross-sectional dimension in a range of about 1 nm to about 100 nm.
13. The analytical substrate of claim 11 , wherein each metallic nanoparticle of the metallic nanoparticle population comprises at least one ligand bound to a surface of the nanoparticle, the ligand comprising a heteroatom head group bound to the nanoparticle surface and a tail bound to the heteroatom head group.
14. The analytical substrate of claim 11 , wherein the metallic nanoparticle population further comprises particle agglomerate comprised of two or more individual nanoparticles, nanoparticle floc comprised of two or more individual nanoparticles, or any combination thereof.
15. The analytical substrate of claim 14 , wherein the ratio, by weight, of the population of individual metallic nanoparticles to particle agglomerate is in the range of from about 1:99 to 99:1.
16. The analytical substrate of claim 14 , wherein the ratio, by weight, of the population of individual metallic nanoparticles to particle floc is in the range of from about 1:99 to 99:1.
17. The analytical substrate of claim 14 , where the nanoparticle agglomerate has an average cross-sectional dimension in the range of from about 100 nm to about 10000 nm.
18. The analytical substrate of claim 14 , wherein the nanoparticle floc has an average cross-sectional dimension in the range of from about 100 nm to about 10000 nm.
19. The analytical substrate of claim 11 , wherein the substrate comprises paper.
20. The analytical substrate of claim 11 , wherein the at least one metallic nanoparticle structure amplifies the Raman signal by a factor less than 1,000,000.